Thqkinetics of the crystallization of isotactic polvlbuteqe from the melt and of the transformation of modification 2 to modification 1 are studied by dilatometric measurements. The isotherms of the polymorphous solid-solid transformation show substaiitially the same features as those of crystallization. Consequently, the transformation was analyzed in terms of AVRAMI'S eqoation. Thc exponent n is 3.1 for c:ystallization, and 3.3 for the solid-solid transformation.Specific volume us. temperature results are reported, and the transformation of modification 2 to modification 1 is shown to be actually possible only below the dilatometric isophasic transition at 65 "C., specific for modification 2. ZUSAMMENFASSUNG:Hit Hilfe von Dilatometermessungen wurdc bei isotaktischem Polybutylen-1 die Kinetik der Kristallisation aus der Schmelze sowie dcr Umwandlung dsr Modifikation 2 in die Modifikation 1 untersucht. Die Isothermen der polymorphen Umwandlung im festen Zustand zeigen im wesentlichen den gleichen Verlauf wie die der Kristallisation. Zur Deutung der Kinetik der Umwandlung wurde die Theorie von AVRAMI herangezogen. Als Exponent ergab sich fur die Kristallisation ein Wert von n = 3,l und fur die Umwandlung ein solcher von n = 3,3.Es wird iiber den Verlauf des spez. Volumens mit der Temperatur berichtet und pezeigt, daB die Umwandlung der Modifikation 2 in die Modifikation 1 nur unterhalb von 65 "C, der Temperatur des fur die Modifikation 2 charakteristischen Phasenuhergangs moglich ist.