No abstract

The mechanisms underlying the effects of nano-calcium carbonate (NC) on the strength of high volume fly ash (FA) mortar are discussed. Two NCs are used as 2%, 4%, 6%, and 8% by weight of cementitious materials. Hydrated products of fly ash mortar containing NC was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TG) and differential thermal gravity (DTG) analysis. Results indicate that NC could improve strength of FA mortar due to the more rapid growth of hydrated products induced by NC through additional nucleation sites. Corresponding to the highest measured strength of FA mortar, the optimal contents of NC are around 2%. In addition, the presence of 2% NC improved the microstructure of FA mortar after 180 days due to the formation of calcium carbonaluminate hydrate.

The calcium leaching behavior of cement paste and silica fume modified calcium hydroxide paste, exposed to hydrochloric acid solution, is reported in this paper. The kinetic of degradation was assessed by the changes of pH of hydrochloric acid solution with time. The changes of compressive strength of specimens in hydrochloric acid with time were tested. Hydration products of leached specimens were also analyzed by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetric (TG), and atomic force microscope (AFM). Tests results show that there is a dynamic equilibrium in the supply and consumption of calcium hydroxide in hydrochloric acid solution, which govern the stability of hydration products such as calcium silicate hydrate (C-S-H). The decrease of compressive strength indicates that C-S-H are decomposed due to the lower concentration of calcium hydroxide in the pore solution than the equilibrium concentration of the hydration products. Furthermore, the hydration of unhydrated clinker delayed the decomposition of C-S-H in hydrochloric acid solution due to the increase of calcium hydroxide in pore solution of cementitious materials.

Economic development and infrastructure improvement will inevitably lead to the accumulation of construction waste and tailings, which has not only a huge impact on the environment but is also a waste of resources. Recycling these resources and making green concrete is an effective way to solve these problems. In this study, the salt spray erosion characteristics and erosion mechanism of tailings recycled concrete (TRC) with polypropylene fibers were studied through macro and micro methods. The results showed that its compressive strength and splitting tensile strength increased at first and then decreased, with the optimum content of 0.6–0.9%, and the strength increase coefficient reached its maximum value at the erosion period being 14 d to 28 d. Under the same erosion cycle, when the fiber content was low (≤0.6–0.9%), the erosion depth hardly fluctuated. While the fiber content changed from 0.6% to 1.2%, the erosion depth and curing ability (erosion for 90 days) increased by 16.29% and 11.20%, which implied that its erosion resistance decreased sharply. Through SEM microscopic analysis, it could be observed that when the fiber content was low, the matrix structure and porosity had little change; while the fiber content was excessive, the porosity increased greatly. The longer the erosion period was, the greater the cumulative expansion of salt crystals was, and the larger the porosity was, whose results were in good agreement with the experimental results. This research provides a significant theoretical basis for the application of TRC in engineering.

Blast furnace ferronickel slag (BFFS) is generated in the production of ferronickel alloys and is used as cement replacement in concrete or mortar. The effectivity in reducing cement consumption and improving performance are limited. By referring to the paste replacement method, this work used BFFS to replace an equal volume of the white Portland cement paste to obtain greater performance enhancement. BFFS was used with five levels of replacement (0%, 5%, 10%, 15%, 20%) and four water-to-cement ratios (0.40, 0.45, 0.50, 0.55) were designed. Fluidity, mechanical strength, hydration products, and pore structure of every mixture were measured. The results showed that the workability of the mortars decreased due to the reduced volume of water, but the 28-day compressive strength of the mortars increased, and the cement content of the mortars was also reduced by 33 wt %. The X-ray diffraction (XRD) patterns revealed that there existed a carboaluminate phase, and the presence of the ettringite was stabilized, indicating that the accumulating amount of the hydration products of the mortar increased. Furthermore, the BFFS could consume the portlandite and free water to form a higher amount of chemically bound water due to its pozzolanic activity. A high degree of hydration and a large volume of the hydration products refined the porosity of the hardened mortars, which explained the enhancement of the strength of the mortars. Compared to the cement replacement method, the paste replacement method was more effective in preparing eco-friendly mortar or concrete by recycling BFFS for reducing the cement content of the mortar while improving its strength.