The main purpose of this paper is to investigate the effect of alkaline treatment on the physical, thermal, mechanical and chemical properties of pristine lemba leaves fibres (LeLeFs). LeLeFs were treated with 6, 8, and 10 wt% sodium hydroxide (NaOH) solution at room temperature for 24 h. In order to determine the functional group presence after the alkaline treatment, LeLeFs were analyzed using Fourier Transform Infrared (FTIR) Spectroscopy. The density of LeLeFs treated with 10 wt% NaOH solution recorded the highest density with 1.168 g/cm³. Morphology study showed that the diameter of fibre reduced with the increment of NaOH concentration. The removal of lignin and hemicellulose could be observed in the thermogravimetric analysis (TGA). Alkaline treatment enhanced the tensile properties of fibre and 10 wt% alkaline treated fibre resulted in the highest tensile strength, modulus and elongation of the fibre at 511.10 MPa, 11.76 GPa and 3.69% respectively. Chemical resistance analysis found that the treated fibre had better chemical resistance compared to untreated fibre. Therefore, it is substantiated that alkaline treatment affects the properties of LeLeF.

This paper presents the effect of UV-LED and UV-mercury as the light source toward curing behaviour of urethane acrylate coating. The UV-curable coating was prepared based on aliphatic urethane acrylate oligomer, 2-ethylhexyl acrylate (2-EHA), methyl methacrylate (MMA), trimethylolpropane triacrylate (TMPTA), and commercial photoinitiator. The effect of irradiation time on curing behaviour was investigated using Fourier Transform Infra-Red (FTIR) and the percentage of C=C conversion was calculated. From the ATR-FTIR spectra, the C=C absorption peak at 810 cm-1 and 1635 cm-1 was found to be decreased after UV irradiation, indicated the proceeding of the polymerisation reaction. In term of C=C conversion, UV-LED irradiation showed better results with 97-99% than UV-mercury irradiation which is 86-96%. It was also observed that the tackiness of the coating reduced via UV-LED irradiation, suggesting higher conversion of monomers. Gel fraction of the coating also measured and higher gel fraction values, > 98% in this study was associated with higher cross-linking density. The results of this study depicted that UV-LED is a viable alternative to replace UV-mercury-based lamp in the coating industry.