ABSTRACT:The effects of various types of compatibilizers on the mechanical properties of high-density polyethylene/ wood flour composites were investigated. Functionalized polyolefins, including maleated polyethylenes, polypropylene, and styrene-ethylene/butylene-styrene copolymer, were incorporated to reduce the interfacial tension between the polyethylene matrix and wood filler. Of these, maleated linear lowdensity and high-density polyethylenes gave higher tensile and impact strengths for the composites, presumably because of their better compatibility with the high-density polyethylene matrix. Similar but less enhanced improvements in the mechanical properties, depending on the compatibilizer loading, were seen for a maleated styrene-ethylene/butylene-styrene triblock copolymer, whereas maleated polypropylene only slightly improved the tensile modulus and tensile strength, which increased with increasing compatibilizer loadings. Scanning electron microscopy was used to reveal the interfacial region and confirm these findings. Dynamic mechanical thermal measurements showed the interaction between the filler and the matrix. Fourier transform infrared spectroscopy was used to assign the chemical fixation and the various chemical species involved on the surfaces of the fillers before and after surface treatment.
The effects of various types of compatibilizers on the mechanical properties of high‐density polyethylene/wood flour (HDPE/WF) composite were investigated. Functionalized polyolefins such as maleated and acrylic acid grafted polyethylenes, maleated polypropylene (PPgMA) and styrene‐ethylene/butylene‐styrene triblock copolymer (SEBSgMA) were incorporated to reduce the interfacial tension between the polyethylene matrix and the wood filler. Among them, it was found that maleated linear low‐density polyethylene (LLDPEgMA) gave maximum tensile and impact strength of the composites, presumably because of better compatibility with the HDPE matrix. Similar but less enhanced improvements in the mechanical properties, depending on the compatibilizer loading, were seen for the SEBSgMA system. Whereas acrylic acid grafted high‐density polyethylene (HDPEgAA) and maleated polypropylene (PPgMA) only slightly improved tensile modulus and tensile strength; and they both increased with increasing loadings of compatibilizers. A scanning electron microscopic study was employed to reveal the interfacial region and confirm these findings. In addition, dynamical mechanical thermal measurements also revealed the interaction between filler and matrix, and FTIR spectroscopy was used to assign the chemical fixation and the various chemical species involved at the surface of the wood fillers before and after surface treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.