In the present work, non-stoichiometric silicon oxide films (SiOx) deposited using a hot filament chemical vapor deposition technique at short time and simple parameters of depositions are reported. This is motivated by the numerous potential applications of SiOx films in areas such as optoelectronics. SiOx films were characterized with different spectroscopic techniques. The deposited films have interesting characteristics such as the presence of silicon nanoclusters without applying thermal annealing, in addition to a strong photoluminescence after applying thermal annealing in the vicinity of 1.5 eV, which may be attributed to the presence of small, oxidized silicon grains (less than 2 nm) or silicon nanocrystals (Si-nc). An interesting correlation was found between oxygen content, the presence of hydrogen, and the formation of defects in the material, with parameters such as the band gap and the Urbach energies. This correlation is interesting in the development of band gap engineering for this material for applications in photonic devices.

This work is focused on making a correlation between results obtained by using spectroscopy and microscopy techniques from single and twofold-layer Silicon-Rich Oxide (SRO) films. SRO films single-layer and twofold-layer characterizations were compared considering the conditions as-grown and with thermal treatment at 1100 °C for 60 min in a nitrogen atmosphere. The thickness of the single-layer film is 324.7 nm while for the twofold-layer film it is 613.2 nm; after heat-treated, both thicknesses decreased until 28.8 nm. X-ray Photoelectron Spectroscopy shows changes in the excess-silicon in single-layer SRO films, with 10% in as-grown films and decreases to 5% for the heat-treated films. Fourier Transform Infrared Spectroscopy (FTIR) exhibits three characteristic vibrational modes of SiO2, as well as, the vibrating modes associated with the Si-H bonds, which disappear after the heat treatment. With UV–Vis spectroscopy results we obtained the absorbance and the absorption coefficient for the SRO films in order to calculate the optical bandgap energy (Egopt), which increased with heat-treatment. The energy peaks of the photoluminescence spectra were used to calculate the silicon nanocrystal size, obtaining thus an average size of 1.89 ± 0.32 nm for the as-grown layer, decreasing the size to 1.64 ± 0.01 nm with the thermal treatment. On the other hand, scanning electron microscopy and high-resolution transmission electron microscopy images confirm the thickness of the twofold-layer SRO films as 628 nm for the as-grown layer and 540 nm for the layer with heat-treatment, and the silicon nanocrystal size of 2.3 ± 0.6 nm for the films with thermal treatment.

No abstract

No abstract

MIS-type structures composed of silicon-rich oxide (SRO), thin films deposited by hot filament chemical vapor deposition (HFCVD), show interesting I-V and I-t properties under white light illumination and a response as photodetectors. From electrical measurements, it was found that at a reverse bias of −4 V, the illumination current increased by up to three orders of magnitude relative to the dark current, which was about 82 nA, while the photogenerated current reached a value of 25 μA. The reported MIS structure with SRO as the dielectric layer exhibited a hopping conduction mechanism, and an ohmic conduction mechanism was found with low voltage. I-t measurements confirmed the increased photogenerated current. Furthermore, the MIS structure, characterized by current-wavelength (I-λ) measurements, exhibited a maximum responsivity value at 254 mA/W, specific detectivity (D*) at 2.21 × 1011 cm Hz1/2 W−1, and a noise equivalent power (NEP) of 49 pW at a wavelength of 535 nm. The structure exhibited good switching behavior, with rise and fall times between 120 and 150 ms, respectively. These rise and decay times explain the generation and recombination of charge carriers and the trapping and release of traps, respectively. These results make MIS-type structures useful as photodetectors in the 420 to 590 nm range.