EFFECT OF CURRENT, TIME, TYPE OF FEED AND CATHODE ON ELECTROPLATING PROCESS OF URANIUM SOLUTION.Electroplating of uranyl nitrate and process effluent has been carried out in order to collect uranium contained therein using Pt/Pt and Pt/SS electrodes at various current and time values. The materials used as electrode were Pt (platinum) and SS (Stainless Steel). Feed solution of 250 mL was entered into a beaker glass equipped with Pt anode -Pt cathode or Pt anode -SS cathode and connected to direct current source from DC power supply at various current values and for various time periods so that uranium precipitated and deposited onto the cathode. Upon deposition completion, the cathode was removed and weighed to determine weight of precipitates, while the solution was analyzed to determine uranium concentration decrease after electroplating process. The experiment shows that a relatively good time to acquire uranium deposit at the cathode was 1 hour at 7 ampere, with uranyl nitrate as feed and Pt (platinum) as cathode. In these conditions, uranium deposit attached to the cathode amounted to 74.96% of the original weight of uranium oxide in the feed or 206.5 mg by weight. The use of Pt cathode for uranyl nitrate feed, and SS and Pt cathodes for effluent feed resulted in uranium specific weight at the cathode of 12.99 mg/cm2, 2.4 mg/cm 2 and 5.37 mg/cm 2 respectively for 7 Ampere current for 1 hour electroplating time.Keywords: electroplating, uranyl nitrate, effluent process, Pt/Pt electrode, Pt/SS electrode.

ABSTRAK PROSES EKSTRAKSI-STRIPPING UO2(NO3)2 BERIMPURITAS HASIL PELARUTAN DARI YELLOW CAKE.Uranil nitrat/UO2(NO3)2 merupakan bahan dasar atau umpan yang dipakai sebagai bahan bakar baik reaktor riset maupun reaktor daya. Di dalam UO2(NO3)2 masih terdapat impuritas sehingga untuk mendapatkan larutan UO2(NO3)2 yang memenuhi persyaratan sebagai bahan bakar murni nuklir (nuclear grade) perlu dilakukan pemurnian dengan menggunakan metode ekstraksi-stripping. Metode ekstraksi stripping dilakukan dengan menggunakan 3 (tiga) parameter yaitu laju alir umpan, keasaman umpan pada proses ekstraksi, dan keasaman. Mekanisme proses ekstraksi menyebabkan UO2(NO3)2 masuk ke dalam fasa organik TBP (tributylphospat), sedangkan impuritasnya berada dalam fasa air (rafinat). Pemungutan uranium dalam fasa organik dilakukan dengan proses stripping dengan cara menentukan keasaman (sebagai parameter), sehingga diperoleh larutan campuran UO2(NO3)2 murni nuklir (nuclear grade). Larutan uranil nitrat hasil pelarutan dengan kadar uranium 225,6282 gU/liter digunakan sebagai umpan. Hasil proses ekstraksi diperoleh laju alir umpan sebesar 15 L/jam, keasaman umpan pada proses ekstraksi sebesar 3 M dan diperoleh kadar uranium sebesar 48,5365 gU/L, sedangkan melalui proses stripping diperoleh UO2(NO3)2 sebesar 64,7860 gU/L pada keasaman 0,04 M.Kata Kunci: ekstraksi, stripping, laju alir umpan, perbandingan TBP/kerosin, keasaman.

Penggunaan meotde elektrodialisis dalam pemisahan uranium dari efluen proses. Percobaan pemisahan uranium dari efluen melalui proses elektrodialisis telah dilakukan. Pada pemisahan uranium tersebut digunakan membran tukar ion. Tujuan percobaan ini dilakukan untuk mengambil uranium dari efluen yang masih memiliki kadar uranium cukup tinggi yaitu di atas 50 ppm. Percobaan dilakukan di dalam sel elektrolitik dua bilik anoda dan katoda yang terbuat dari bahan flexiglass. Membram tukar ion diselipkan di antara dua bilik. Uranium dapat dipisahkan dari efluen proses hingga 100% pada tegangan 3,5 volt selama 3,67 jam. Pada proses elektrodialisis untuk memisahkan uranium berkandungan hasil berupa penurunan Fluor hingga 78%.