Two different zinc-based metal-organic frameworks (MOFs) were investigated to remove one of the most used fluoroquinolone antibiotic, Ofloxacin (OFL), from polluted water. The most common zeolitic imidazolate framework-8 (ZIF-8) and the green Zn(II) and benzene-1,3,5-tri-carboxylate (Zn3(BTC)2) were prepared through a facile synthetic route and characterized by means of Fourier-Transform Infrared (FT-IR) Spectroscopy, X-ray Powder Diffraction (XRPD), and Scanning Electron Microscopy (SEM) analyses. The two MOFs were compared in terms of both adsorption and kinetic aspects under real conditions (tap water, natural pH). Results showed that OFL was adsorbed in remarkable amounts, 95 ± 10 and 25.3 ± 0.8 mg g−1 on ZIF-8 and Zn3(BTC)2, respectively, following different mechanisms. Specifically, a Langmuir model well described the ZIF-8 profile, while for Zn3(BTC)2, cooperative adsorption occurred. Moreover the kinetic results were quite different, pseudo-second-order and sigmoidal, respectively. The suitability of ZIF-8 and Zn3(BTC)2 as adsorbent phases for water depollution was tested on tap water samples spiked with OFL 10 µg L−1. The obtained removal efficiencies, of 88% for ZIF-8 and 72% for Zn3(BTC)2, make these materials promising candidates for removing fluoroquinolone antibiotics (FQs) from polluted waters, notwithstanding their limited reusability in tap water, as demonstrated by in-depth characterization of the two MOFs after usage.

A simple not solvent and time consuming Fe3O4@MIL-100(Fe), synthesized in the presence of a small amount of magnetite (Fe3O4) nanoparticles (27.3 wt%), is here presented and discussed. Layer-by-layer alone (20 shell), and combined layer-by-layer (5 shell)/reflux or /hydrothermal synthetic procedures were compared. The last approach (Fe3O4@MIL-100_H sample) is suitable (i) to obtain rounded-shaped nanoparticles (200–400 nm diameter) of magnetite core and MIL-100(Fe) shell; (ii) to reduce the solvent and time consumption (the layer-by-layer procedure is applied only 5 times); (iii) to give the highest MIL-100(Fe) amount in the composite (72.7 vs. 18.5 wt% in the layer-by-layer alone); (iv) to obtain a high surface area of 3546 m2 g−1. The MIL-100(Fe) sample was also synthesized and both materials were tested for the absorption of Ofloxacin antibiotic (OFL). Langmuir model well describes OFL adsorption on Fe3O4@MIL-100_H, indicating an even higher adsorption capacity (218 ± 7 mg g−1) with respect to MIL-100 (123 ± 5 mg g−1). Chemisorption regulates the kinetic process on both the composite materials. Fe3O4@MIL-100_H performance was then verified for OFL removal at µg per liter in tap and river waters, and compared with MIL-100. Its relevant and higher adsorption efficiency and the magnetic behavior make it an excellent candidate for environmental depollution.

In this work, red mud (RM) and spinel iron oxide nanoparticles (SPIONs) were added to pure silica/alumina sources (SAs) and fly ash (FA) with the aim of synthesizing and investigating the magnetic behavior of different zeolites. SAs were used to synthesize zeolite with LTA topology (zeolite A) with the addition of both red mud and spinel iron oxide nanoparticles. FA and RM were mixed to synthesize sodalite whereas only FA with the addition of SPIONs was used to form zeolite with FAU-topology (zeolite X). All the synthetic products showed magnetic properties. However, zeolites with spinel iron oxide nanoparticles (zeolites A and X) showed ferromagnetic-like behavior. Sodalite was characterized by a reduction in saturation magnetization, whereas zeolite A with red mud displayed antiferromagnetic behavior. For the first time, all the synthetic products were tested for polluted water remediation by a persistent emerging contaminant, ofloxacin (OFL) antibiotic. The four zeolite types showed good adsorption affinity towards OFL under actual conditions (tap water, natural pH). All materials were also tested for OFL removal in real waters spiked with OFL 10 µg L−1. Satisfactory recoveries (90–92% in tap water, 83–87% in river water) were obtained for the two zeolites synthesized from industrial waste materials.