Corrosion of the nitinol wire in endovascular grafts is confirmed. Presumably, the observed pitting and irregularly shaped corrosion defects are the precursors of material failure. They weaken the thin wire, which leads to stress cracks and eventually fracture of the stent wire under circulatory pulsation. Cell-induced electrochemical corrosion and active cellular destruction of surfaces are well-known mechanisms that must be investigated for their possible roles in the corrosion of stent metals.

Regular follow-ups of patients with aged vascular grafts and the precise documentation of implanted materials are necessary to estimate graft degradation.

Continuous movements in the grafted aorta and blood pressure impose permanent stress to the stent frame and the polyester fabric resulting in morphological changes in the body middle ring of grafts. The clinical implications of the suture breakages are unknown although they may be related to distal secondary leakage in tube grafts.

Holes in the polyester fabric and frame dislocations are specific for the design of Stentor and Vanguard grafts. The early corrosion of the stent metal Nitinol in these devices is surprising. Until more experience is gained with other devices, we have to be reminded, that the "gold standard" for the long-term durability of artificial vascular grafts is still "today's" conventional graft.

In this study, we have identified a specific mechanism of late (9-20 years) longitudinal rupture of knitted polyester prostheses consisting of degradation of the polyester filaments along the remeshing and guide lines that run the length of the graft.