A novel main-chain polyfullerene, poly[fullerene-alt-2,5-bis(octyloxy)terephthalaldehyde] (PPC4), is investigated for its hypothesized superior morphological stability as an electron-accepting material in organic photovoltaics relative to the widely used fullerene phenyl-C61-butyric acid methyl ester (PCBM). When mixed with poly(3-hexylthiophene-2,5-diyl) (P3HT), PPC4 affords low-charge-generation yields because of poor intermixing within the blend. The adoption of a multiacceptor system, by introducing PCBM into the P3HT:polyfullerene blend, was found to lead to a 3-fold enhancement in charge generation, affording power conversion efficiencies very close to that of the prototypical P3HT:PCBM binary control. Upon thermal stressing and in contrast to the P3HT:PCBM binary, photovoltaic devices based on the multiacceptor system demonstrated significantly improved stability, outperforming the control because of suppression of the PCBM migration and aggregation processes responsible for rapid device failure. We rationalize the influence of the fullerene miscibility and its implications on the device performance in terms of a thermodynamic model based on Flory-Huggins solution theory. Finally, the potential universal applicability of this approach for thermal stabilization of organic solar cells is demonstrated, utilizing an alternative low-band-gap polymer-donor system.

Fullerene is used as a monomer in this simple method to prepare soluble, well-defined polymers. The sterically controlled azomethine ylide cycloaddition polymerization of fullerene (SACAP) yields macromolecules with molecular weights of around 25 000 g mol −1 . Importantly, cumbersome comonomers are employed to restrict crosslinking. Extensive characterizations, with the help of modeling studies, indicate that the polymers are regio-irregular with a majority of trans-3 isomers. Of particular interest is the exceptional ease of preparing polymers with zero metal content.

Polymer/metal nanocomposite containing intrinsically anisotropic metal nanostructures such as metal nanorods and nanowires appeared extremely more sensitive and responsive to mechanical stimuli than nanocomposites containing spherical nanoparticles. After uniaxial stretching of the supporting polymer matrix (poly(vinyl alcohol)), the elongated silver nanostructures embedded at low concentration into the polymer matrix (<1 wt % of Ag) assume the direction of the drawing, yielding materials with a strong dichroic response of the absorption behavior. Accordingly, the film changed its color when observed under linearly polarized light already at moderate drawings. The results obtained suggest that nanocomposite films have potential in applications such as color polarizing filters, radiation responsive polymeric objects and smart flexible films in packaging applications.