No abstract

BioUnion filler is a bioactive glass particle that releases Zn 2+ in an acidic environment. In this study, the ion release, antibacterial, and physical properties of a glass ionomer cement (GIC) incorporating BioUnion filler (CA) were assessed in vitro. The concentration of Zn 2+ released from CA into acetic acid was higher than that released into water and its minimum inhibitory concentrations against six oral bacterial species. Moreover, the concentration of Zn 2+ -release was maintained during all the seven times it was exposed to acetic acid. Compared to a conventional cement and resin composite, CA significantly inhibited the growth of oral bacteria and hindered their adhesion on the material surface. Thus, our study outcomes show that the release of Zn 2+ from CA in the acidic environment does not affect its compressive strength.

Bone organoids offer a novel path for the reconstruction and repair of bone defects. We previously fabricated scaffold-free bone organoids using cell constructs comprising only bone marrow-derived mesenchymal stem cells (BMSCs). However, the cells in the millimetre-scale constructs were likely to undergo necrosis because of difficult oxygen diffusion and nutrient delivery. Dental pulp stem cells (DPSCs) are capable of differentiating into vascular endothelial lineages and have great vasculogenic potential under endothelial induction. Therefore, we hypothesized that DPSCs can serve as a vascular source to improve the survival of the BMSCs within the bone organoid. In this study, the DPSCs had greater sprouting ability, and the proangiogenic marker expressions were significantly greater than those of BMSCs. DPSCs were incorporated into the BMSC constructs at various ratios (5%–20%), and their internal structures and vasculogenic and osteogenic characteristics were investigated after endothelial differentiation. As a result, the DPSCs are differentiated into the CD31-positive endothelial lineage in the cell constructs. The incorporation of DPSCs significantly suppressed cell necrosis and improved the viability of the cell constructs. In addition, lumen-like structures were visualized by fluorescently labelled nanoparticles in the DPSC-incorporated cell constructs. The vascularized BMSC constructs were successfully fabricated using the vasculogenic ability of the DPSCs. Next, osteogenic induction was initiated in the vascularized BMSC/DPSC constructs. Compared with only BMSCs, constructs with DPSCs had increased mineralized deposition and a hollow structure. Overall, this study demonstrated that vascularized scaffold-free bone organoids were successfully fabricated by incorporating DPSCs into BMSC constructs, and the biomimetic biomaterial is promising for bone regenerative medicine and drug development.

The on-demand release of antibacterial components due to pH variations caused by acidogenic/cariogenic bacteria is a possible design for smart antibacterial restorative materials. This study aimed to fabricate pH-responsive Zn2+-releasing glass particles and evaluate their solubilities, ion-releasing characteristics, and antibacterial properties in vitro. Three kinds of silicate-based glass particles containing different molar ratios of Zn (PG-1: 25.3; PG-2: 34.6; PG-3: 42.7 mol%) were fabricated. Each particle was immersed in a pH-adjusted medium, and the solubility and concentration of the released ions were determined. To evaluate the antibacterial effect, Streptococcus mutans was cultured in the pH-adjusted medium in the presence of each particle, and the bacterial number was counted. The solubility and concentration of Zn2+ released in the medium increased with a decrease in medium pH. PG-3 with a greater content of Zn demonstrated higher concentrations of released Zn2+ compared with PG-1 and PG-2. PG-2 exhibited bactericidal effects at pH 5.1, whereas PG-3 demonstrated bactericidal effects at pH values of 5.1 and 6.1, indicating that PG-3 was effective at inhibiting S. mutans even under slightly acidic conditions. The glass particle with 42.7 mol% Zn may be useful for developing smart antibacterial restoratives that contribute to the prevention of diseases such as caries on root surfaces with lower acid resistance.