Nanosized rod-like, wire-like, and tubular α-MnO(2) and flower-like spherical Mn(2)O(3) have been prepared via the hydrothermal method and the CCl(4) solution method, respectively. The physicochemical properties of the materials were characterized using numerous analytical techniques. The catalytic activities of the catalysts were evaluated for toluene oxidation. It is shown that α-MnO(2) nanorods, nanowires, and nanotubes with a surface area of 45-83 m(2)/g were tetragonal in crystal structure, whereas flower-like spherical Mn(2)O(3) with a surface area of 162 m(2)/g was of cubic crystal structure. There were the presence of surface Mn ions in multiple oxidation states (e.g., Mn(3+), Mn(4+), or even Mn(2+)) and the formation of surface oxygen vacancies. The oxygen adspecies concentration and low-temperature reducibility decreased in the order of rod-like α-MnO(2) > tube-like α-MnO(2) > flower-like Mn(2)O(3) > wire-like α-MnO(2), in good agreement with the sequence of the catalytic performance of these samples. The best-performing rod-like α-MnO(2) catalyst could effectively catalyze the total oxidation of toluene at lower temperatures (T(50%) = 210 °C and T(90%) = 225 °C at space velocity = 20,000 mL/(g h)). It is concluded that the excellent catalytic performance of α-MnO(2) nanorods might be associated with the high oxygen adspecies concentration and good low-temperature reducibility. We are sure that such one-dimensional well-defined morphological manganese oxides are promising materials for the catalytic elimination of air pollutants.

No abstract

The present review article highlights the preparation, characterization, properties, and recent developments in porous metal oxide catalysts for heterogeneous catalysis.

No abstract

Three-dimensionally (3D) ordered macroporous (3DOM) MgO, gamma-Al(2)O(3), Ce(0.6)Zr(0.4)O(2), and Ce(0.7)Zr(0.3)O(2) with polycrystalline mesoporous walls have been successfully fabricated with the triblock copolymer EO(106)PO(70)EO(106) (Pluronic F127) and regularly packed monodispersive polymethyl methacrylate (PMMA) microspheres as the template and magnesium, aluminum, cerium and zirconium nitrate(s), or aluminum isopropoxide as the metal source. The as-synthesized metal oxides were characterized by means of techniques such as X-ray diffraction (XRD), thermogravimetric analysis/differential scanning calorimetry (TGA/DSC), Fourier transform infrared (FT-IR), high-resolution scanning electron microscopy (HRSEM), high-resolution transmission electron microscopy/selected area electron diffraction (HRTEM/SAED), BET, carbon dioxide temperature-programmed desorption (CO(2)-TPD), and hydrogen temperature-programmed reduction (H(2)-TPR). It is shown that the as-fabricated MgO, gamma-Al(2)O(3), Ce(0.6)Zr(0.4)O(2), and Ce(0.7)Zr(0.3)O(2) samples possessed single-phase polycrystalline structures and displayed a 3DOM architecture; the MgO, Ce(0.6)Zr(0.4)O(2), and Ce(0.7)Zr(0.3)O(2) samples exhibited worm-hole-like mesoporous walls, whereas the gamma-Al(2)O(3) samples exhibited 3D ordered mesoporous walls. The solvent (ethanol or water) nature and concentration, metal precursor, surfactant, and drying condition have an important impact on the pore structure and surface area of the final product. The introduction of surfactant F127 to the synthesis system could significantly enhance the surface areas of the 3DOM metal oxides. With PMMA and F127 in a 40% ethanol solution, one can generate well-arrayed 3DOM MgO with a surface area of 243 m(2)/g and 3DOM Ce(0.6)Zr(0.4)O(2) with a surface area of 100 m(2)/g; with PMMA and F127 in an ethanol-HNO(3) solution, one can obtain 3DOM gamma-Al(2)O(3)with a surface area of 145 m(2)/g. The 3DOM MgO and 3DOM gamma-Al(2)O(3) samples showed excellent CO(2) adsorption behaviors, whereas the 3DOM Ce(0.6)Zr(0.4)O(2) sample exhibited exceptional low-temperature reducibility. The unique physicochemical properties associated with the copresence of 3DOM and mesoporous walls make these porous materials ideal candidates for applications in heterogeneous catalysis and CO(2) adsorption.