A thin (2 μm) and relatively large area (3 × 3 mm2) diamond membrane was fabricated by cleaving a surface from a single crystal chemical vapor deposition (CVD) diamond wafer (3 × 3 mm2× 300 μm) using a hot implantation and ion-cut method. First, while maintaining the CVD diamond at 400 °C, a damage zone was created at a depth of 2.3 μm underneath the surface by implanting 4 MeV carbon ions into the diamond in order to promote membrane cleavage (hot implantation). According to TEM data, hot implantation reduces the thickness of the implantation damage zone by about a factor of 10 when compared to implanting carbon ions with the CVD diamond at room temperature (RT). In order to recover crystallinity, the implanted sample was then annealed at 850 °C. Next, 380 keV hydrogen ions were implanted into the sample to a depth of 2.3 μm below the surface with the CVD diamond at RT. After annealing at 850 °C, the CVD diamond surface layer was cleaved at the damage-zone due to internal pressure from H2 gas arising from the implanted hydrogen (ion-cut). A thin layer of graphite (∼300 nm) on the cleavage surface, arising from the implanted carbon, was removed by O2 annealing. This technique can potentially be used to produce much larger area membranes of variable thickness.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.