This paper presents a non-contact printing mechanism for high aspect ratio silver (Ag) electrodes fabricated by an electrohydrodynamic (EHD) jet printing technique. Using high viscosity Ag paste ink, we were able to fabricate narrow and high aspect ratio electrodes. We investigated the effect of the surface energy of the substrate and improved the aspect ratio of printed lines through multiple printing. We fabricated the polycrystalline silicone solar cell with the Ag electrode and achieved cell efficiency of around 13.7%. The EHD jet printing mechanism may be an alternative method for non-contact fabrication of solar cells electrodes.

As a novel route to construct fine and abnormally high-aspect-ratio electrodes with excellent adhesion and reduced contact resistivity on a textured surface, an electrostatic-force-assisted dispensing printing technique is reported and compared with conventional dispensing and electrohydrodynamic jet printing techniques. The electrostatic force applied between a silver paste and the textured surface of a crystalline silicon solar cell wafer significantly improves the physical adhesion of the electrodes, whereas those fabricated using a conventional dispensing printing technique peel off with a silver paste containing 2 wt% of a fluorosurfactant. Moreover, the contact resistivity and dimensionless deviation of total resistance are significantly reduced from 2.19 ± 1.53 mΩ·cm2 to 0.98 ± 0.92 mΩ·cm2 and from 0.10 to 0.03, respectively. By utilizing electrodes with an abnormally high-aspect-ratio of 0.79 (the measured thickness and width are 30.4 μm and 38.3 μm, respectively), the cell efficiency is 17.2% on a polycrystalline silicon solar cell with an emitter sheet resistance of 60 Ω/sq. This cell efficiency is considerably higher than previously reported values obtained using a conventional electrohydrodynamic jet printing technique, by +0.48–3.5%p.

No abstract

A permeability- and surface-energy-controllable polyurethane acrylate (PUA) mold, a "capillary-force material (CFM)" mold, is introduced for capillary-force lithography (CFL). In CFL, the surface energy and gas permeability of the mold are crucial. However, the modulation of these two main factors at a time is difficult. Here, we introduce new CFM molds in which the surface energy and permeability can be modified by controlling the degree of cross-linking of the CFM. As the degree of cross-linking of the CFM mold increases, the surface energy and air permeability decrease. The high average functionality of the mold material makes it possible to produce patterns relatively finely and rapidly due to the high rate of capillary rise and stiffness, and the low functionality allows for patterns to form on a curved surface with conformal contact. CFMs with different functionality and controllable-interfacial properties will extend the capabilities of capillary force lithography to overcome the geometric limitations of patterning on a scale below 100 nm and micro- and nanopatterning on the curved region.