The preparation of polystyrene-coated cobalt oxide nanowires is reported via the colloidal polymerization of polymer-coated ferromagnetic cobalt nanoparticles (PS-CoNPs). Using a combination of dipolar nanoparticle assembly and a solution oxidation of preorganized metallic colloids, interconnected nanoparticles of cobalt oxide spanning micrometers in length were prepared. The colloidal polymerization of PS-CoNPs into cobalt oxide (CoO and Co(3)O(4)) nanowires was achieved by bubbling O(2) into PS-CoNP dispersions in 1,2-dichlorobenzene at 175 degrees C. Calcination of thin films of PS-coated cobalt oxide nanowires afforded Co(3)O(4) metal oxide materials. Transmission electron microscopy (TEM) revealed the formation of interconnected nanoparticles of cobalt oxide with hollow inclusions, arising from a combination of dipolar assembly of PS-CoNPs and the nanoscale Kirkendall effect in the oxidation reaction. Using a wide range of spectroscopic and electrochemical characterization techniques, we demonstrate that cobalt oxide nanowires prepared via this novel methodology were electroactive with potential applications as nanostructured electrodes for energy storage.

The preparation of cobalt oxide nanowires with gold nanoparticle (AuNP) inclusions (Au-Co(3)O(4) nanowires) via colloidal polymerization of dipolar core-shell NPs is reported. Polystyrene-coated ferromagnetic NPs composed of a dipolar metallic cobalt shell and a gold NP core (PS-AuCoNPs) were synthesized by thermolysis of octacarbonyldicobalt [Co(2)(CO)(8)] in the presence of AuNP seeds and polymeric ligands. The colloidal polymerization process of these dipolar PS-AuCoNPs comprises dipolar nanoparticle assembly and solution oxidation of preorganized NPs to form interconnected cobalt oxide nanowires via the nanoscale Kirkendall effect, with AuNP inclusions in every repeating unit of the one-dimensional mesostructure. Calcination of the polymer-coated nanowires afforded polycrystalline Au-Co(3)O(4) nanowires that were determined to be electroactive. Nanocomposite materials were characterized by transmission electron microscopy, field-emission scanning electron microscopy, X-ray diffraction, vibrating sample magnetometry, and cyclic voltammetry. We demonstrate that the optical and electrochemical properties of Au-Co(3)O(4) nanowires are significantly enhanced in comparison with hollow Co(3)O(4) nanowires prepared via colloidal polymerization.