Bracket failure is one of the most important problems encountered during fixed orthodontic treatment. For this reason, different types of adhesive agents have been developed over the years. Consequently, the aim of this study was to evaluate the shear bond strength of brackets bonded to teeth etched with a conventional acid etching method in a laboratory environment by using different types of adhesive agents and comparing the number of shear strokes. Sixty human maxillary premolars were divided into three groups and Gemini stainless steel metal brackets (3M Unitek, Monrovia, CA, USA) were bonded to all teeth. In Group 1, Transbond™ XT Primer (3M Unitek, Monrovia, CA, USA) and Transbond™ XT Light Cure Adhesive Paste composite (3M Unitek, Monrovia, CA, USA) were used. In Group 2, BracePaste® MTP Primer (American Orthodontics, Sheboygan, CA, USA) and BracePaste® Adhesive composite (American Orthodontics, Sheboygan, WI, USA) were used. In Group 3, Ortho Solo™ Primer (Ormco, Orange, CA, USA) and Grengloo™ Adhesive composite (Ormco, Brea, CA, USA) were used. The samples were subjected to a shear test with a closed-loop controlled, low-cycle fatigue machine with a capacity of 10 N and a crosshead speed of 300 mm/min. The number of shear strokes of the brackets was recorded. According to the Kruskal–Wallis and Mann–Whitney U tests performed on the data obtained, statistically significant differences were found between the groups in terms of the numbers of shear strokes (p < 0.05). Significantly higher numbers of shear strokes and higher shear bond strengths were observed in Group 3 compared with Group 1 and Group 2 (p < 0.05). There was no statistically significant difference between the numbers of shear strokes for Group 1 and Group 2 samples (p > 0.05). To conclude the study, it was observed that the type of adhesive used had an effect on the bond strength of the bracket and that the Grengloo™ adhesive agent showed higher shear bond strength. It was observed that BracePaste® Adhesive and Transbond™ XT Light Cure Adhesive Paste adhesive agents had similar shear bond strengths.