Epoxy composites filled with 0.5 wt% of multi-walled carbon nanotubes (MWCNTs), 10 and 15 wt% of boric acid and sodium bicarbonate separately, as well as composites filled with a combination of MWCNTs-boric acid and MWCNTs-sodium bicarbonate were prepared. The thermal behavior of the prepared samples was investigated under heating in oxidative environment using thermogravimetric analysis. The hardness was measured using the Shore D hardness test. To evaluate the flammability of the samples, the ignition temperature and time-to-ignition were determined. It was concluded that sodium bicarbonate in the studied concentrations (10 and 15 wt%) is not appropriate for use as a filler capable of improving the thermooxidative stability and reducing the flammability of epoxy polymers. The improvement in the thermal properties can be achieved by using the combination of boric acid and multi-walled carbon nanotubes as fillers. The thermooxidative destruction of the samples filled with boric acid passes more slowly and more evenly via the formation of B2O3 as a result of its decomposition.

Reduction of flammability and improvement of thermal stability of polymers during heating can be achieved by the introduction of fillers. Epoxy composites filled with different loadings of multi-walled carbon nanotubes (MWCNTs) and expanded graphite (EG) were prepared. The thermal oxidation stability of the prepared samples was investigated under heating in an oxidizing atmosphere using thermal analysis. The hardness was measured using the Shore D hardness test. The flammability of the prepared composites was evaluated by the ignition temperature and time-to-ignition. It was found that there was a rise in temperature corresponding to a 5% weight loss during heating for both epoxy/MWCNT and epoxy/EG composites compared to neat epoxy resin. The Shore D hardness of epoxy/MWCNT composites increased with content growth up to 0.1 wt.% and decreased with further concentration rise. The addition of MWCNTs and EG leads to an increase in the ignition temperature. It has been shown that MWCNTs improve the thermal behavior of epoxy resin in a low temperature region (below ~ 300 °C) whereas EG shows almost the same thermal behavior above 300 °C. The improvement of thermal properties can be achieved using MWCNTs and EG as fillers.

No abstract

No abstract