The phototransferred thermoluminescence (PTTL) technique is applied to the Harshaw LiF:Mg,Cu,P material. It is demonstrated that using 254-nm UV light, dose levels as low as 0.2 mGy can be re-estimated. The PTTL efficiency was found to be ∼ 6 % in the dose range of 0.2 mGy-1 Gy, and it appears to be dose-independent. This implies that a simple calibration factor could be applied to the PTTL data for the re-estimation of dose levels. It was demonstrated that with a proper choice of the TL readout parameters, and the UV-light irradiation conditions, dose levels that are relevant to personal or environmental dosimetry can be re-estimated.

<p>Ba_0,8Sr_0,2TiO₃was made by co-precipitation method with the sintering temperature of 600^oC, 700^oC, 800^oC and 900^oC for 4 hours. Sintering temperature was varied to investigate its effect on microstructure and dielectric constant of Ba_0,8Sr_0,2TiO₃. microstructure characterization was performed by X-Ray Diffraction (XRD) instrument. Dielectric constant characterization was perform by LCR meter. The crystal size increased significantly with increasing sintering temperature. Measurements of dielectric constant were performed at range of frequency 0.01 to 100 KHz. Dielectric constant value is highest at the lowest frequency. Dielectric constant value size increased significantly with increasing sintering temperature.</p>

The effects of UV-induced bleaching of deep traps on Harshaw thermoluminescent (TL) LiF:Mg,Cu,P and LiF:Mg,Ti materials were investigated. During a normal heating cycle, LiF:Mg,Cu,P is limited to a maximum temperature of 240 °C. LiF:Mg,Ti can be read to higher temperatures; however, encapsulation in polytetrafluoroethylene limits the maximum readout temperature to 300 °C. Generally, for both materials, these respective temperatures are sufficient for emptying traps corresponding to the main dosemetric peaks. However, when the dosemeters are subjected to a high dose level, such as 1 Gy (much higher than individual monitoring dose levels), higher temperature traps are filled that cannot be emptied without exceeding the above-mentioned maximum temperatures. These high temperature traps tend to be unstable during normal readout and can significantly increase the residual TL signal. The purpose of this study was to investigate the applicability of a UV-induced bleaching technique for emptying higher temperature traps following high-dose applications. In addition, in the case of LiF:Mg,Cu,P, where the maximum readout temperature is significantly lower, we investigated the possibility of reducing the residual signal using the application of repeated readout cycles. The optical bleaching approach was found to be effective in the case of LiF:Mg,Ti; however, for LiF:Mg,Cu,P, no reduction in the residual signal was observed. For this latter material, the application of repeatable readout cycles is very effective and residual signals equivalent to dose levels as low as 0.01 mGy were observed following an initial dose of 5 Gy. To the best of our knowledge, this work is the first attempt to apply an 'optical annealing' technique to the Harshaw thermoluminescent dosemeter (TLD) materials.