In this work, studies have been carried out to replace bauxite with aluminate slags. Compounds of raw mixtures without use of fossil aluminate materials with different gypsum content have been developed. Instability of assimilation of anhydrite into calcium sulphoaluminate has been established. X-ray phase analysis has shown a weak dependence of increase in the firing temperature and increase in the yield of the main mineral C3A3·CŜ. Results of the study allow us to conclude that it is possible to obtain high-quality calcium sulphoaluminate (SAC) based on technogenic aluminate raw material.

No abstract

This paper deals with the composition and properties of solid solution of calcium sulfoferrite. It was studied an influence of calcium s sulfoferrite on structure and properties cement phases. Study of the hydration processes of the calcium sulfoferrite mineral are observed only short prismatic crystals. Prismatic crystals of ferruginous ettringite are always formed from sulfoferrite mineral of any fraction. it was found that the smaller the initial hydrating grains of minerals, the faster they are hydrated. Analyse polyfractional compound hydration showed that fine fractions provide formation of crystallization centres, and particles less than 45 microns, with constant interaction with the liquid phase, cause a gradual growth of crystals. Expansion of hydrated minerals of certain fractions was analysed to check the dependence of the expansion on the morphology of ettringite crystal hydrates. During the hardening of the samples, expansion was observed along with a drop in strength.