In this work, dielectric spectroscopy was conducted on five commercial woven polypropylene‐based fabrics. Measurements of dielectric loss tangent, the effective relative dielectric permeability and ac electrical conductivity were performed over a wide range of temperature and frequency. The results in temperature range from 250 K to 355 K showed that the samples with lower value of volume fraction whose yarn is made from a short fiber have a lower value of the above mentioned dielectric parameters than the samples with bigger value of volume fraction and filament yarn along the weft and the warp lines. Based on the results gained from the measurements in the vacuum and ambient conditions, it can be concluded that the samples with a lower value of volume fraction, whose yarn is made from a short fiber, showed stability of dielectric properties in the measurement interval. Copyright © 2014 John Wiley & Sons, Ltd.

In this study, the effects of doping by 3d (V, Mn, Fe, Ni) and 4f (Nd, Sm, Er) ions on dielectric and infrared properties of SrTiO 3 (STO) single crystals are investigated. It is well known that doping of the SrTiO 3 can change the dielectric properties of the STO from an insulator to an n-type semiconductor, and even to a metallic conductor. Dielectric and infrared (IR) properties of the undoped STO and doped STO single crystals are analyzed using dielectric spectroscopy (80 kHz-5 MHz), transmission (200 cm −1 -4000 cm −1 ), and reflection spectroscopy (50 cm −1 -2000 cm −1 ). It is found that doping by the 3d ions reduces the value of dielectric permittivity, but the trend of temperature dependence of the dielectric permittivity remains almost unchanged. On the other hand, dielectric spectroscopy measurements for samples doped by 4f ions show the anomalous behaviors of the dielectric permittivity at temperatures around the temperature of the structural phase transition. There are two fractures of temperature dependences of inverse dielectric permittivity ε −1 r (T ). Transmittance spectroscopy measurements show that there are differences in the shape of the spectrum in the mid-IR region between the undoped STO and the one doped by 4f ions. The differences in the reflectance spectrum between the STO:Nd and STO are analyzed in detail.

No abstract

No abstract

In this paper, a new simple and environmentally friendly treatment technique for obtaining polymer nanocomposites with appropriate dielectric properties has been presented. Sheets of isotactic polypropylene and atactic polystyrene were immersed in 3 saturated water solutions of alkali metal salts (LiCl, NaCl, and KCl) at 2 fixed temperatures (23°C and 90°C), and 3 DC electrical potentials (+4 kV, −4 kV, and ground potential) were applied. A quantification of alkali metals in the polymer sheets was conducted by inductively coupled plasma optic emission spectrometry. The obtained concentration values were from 7.38·10−9 mol/cm3 to 1.25·10−7 mol/cm3. The qualitative analysis of potassium distribution in the polymer matrix was conducted by time‐of‐flight secondary ion mass spectrometry cross‐sectional record. The relative dielectric constant (ε′) of samples was investigated in the frequency range from 20 Hz to 9 MHz at the constant temperature of 22°C. Stable values of ε′ in fully measured frequency range were observed for both pure and treated samples. Next, the results of the dielectric spectroscopy measurements were compared and established the kind of treatment that provided the highest value of ε′. The relationship between the concentrations of alkali metals and the values of relative dielectric constant was determined for the samples obtained by a treatment at 90°C and +4 kV.