Matrix metalloproteinases (MMPs) are enzymes that can degrade collagen in hybrid layer and reduce the longevity of adhesive restorations. As scientific understanding of the MMPs has advanced, useful strategies focusing on preventing these enzymes' actions by MMP inhibitors have quickly developed in many medical fields. However, in restorative dentistry, it is still not well established. This paper is an overview of the strategies to inhibit MMPs that can achieve a long-lasting material-tooth adhesion. Literature search was performed comprehensively using the electronic databases: PubMed, ScienceDirect and Scopus including articles from May 2007 to December 2019 and the main search terms were "matrix metalloproteinases", "collagen", and "dentin" and "hybrid layer". MMPs typical structure consists of several distinct domains. MMP inhibitors can be divided into 2 main groups: synthetic (syntheticpeptides, non-peptide molecules and compounds, tetracyclines, metallic ions, and others) and natural bioactive inhibitors mainly flavonoids. Selective inhibitors of MMPs promise to be the future for specific targeting of preventing dentin proteolysis. The knowledge about MMPs functionality should be considered to synthesize drugs capable to efficiently and selectively block MMPs chemical routes targeting their inactivation in order to overcome the current limitations of the therapeutic use of MMPs inhibitors, i.e., easy clinical application and long-lasting effect.

This study aimed to evaluate effectiveness and effects of bleaching with 35% hydrogen peroxide with and without calcium on color, micromorphology, and the replacement of calcium and phosphate on the enamel surface. Thirty bovine enamel blocks (5.0 × 5.0 mm) were placed into the following groups: G1: artificial saliva (control); G2: 35% hydrogen peroxide gel without calcium (Whiteness HP Maxx-FGM); and G3: 35% hydrogen peroxide gel with calcium (Whiteness HP Blue-FGM). Three color measurements were performed with a spectrophotometer: untreated (baseline), after performing staining, and after application of bleaching agents. Calcium deposition on the enamel was evaluated before and after the application of bleaching agents using energy-dispersive X-ray spectrometry. The enamel surface micromorphology was observed under scanning electron microscopy. The pH of each product was measured. The data were subjected to one-factor analysis of variance (ANOVA), and any differences were analyzed using Tukey's test (P < 0.05). G3 showed greater variation in total color after the experiment than G2 and G1; there was no significant difference in calcium or phosphorus concentration before and after the experimental procedures; morphological changes were observed only in G2 and G3; and the pH values of the Whiteness HP Maxx and Whiteness HP Blue bleaching agents were 5.77 and 7.79, respectively. The 35% hydrogen peroxide with calcium showed greater bleaching potential, but the addition of calcium had no effect in terms of reducing morphological changes or increasing the calcium concentration on the enamel surface.

<p>O objetivo do trabalho foi realizar uma análise crítica do processo de apropriação das patentes em própolis que podem ser consideradas uma proxy de apropriabilidade de valor da inovação, particularmente quando se trata da grande empresa. Realizou-se uma investigação de artigos científicos, documentos de patentes e busca de anterioridade realizados por meio de bases de dados, nacionais e internacionais. A contribuição foi mostrar que o desenvolvimento tecnológico pode acontecer por meio das empresas de Biotecnologia (Biotec), mas os ativos específicos e co-especializados necessários para a proteção do conhecimento de acordo com os regimes de apropriabilidade vigentes, as estratégias para explorar a maior fatia do valor da inovação são traçadas pelas grandes empresas. A originalidade do trabalho vem da própolis como objeto de pesquisa que apesar de bastante conhecida e utilizada no exterior ainda é pouco estudada em termos de redes de pesquisa e inovação no Brasil.</p>