We have studied the role of defects in electrolyte-gated graphene mesh (GM) field-effect transistors (FETs) by introducing engineered edge defects in graphene (Gr) channels. Compared with Gr-FETs, GM-FETs were characterized as having large increments of Dirac point shift (∼30-100 mV/pH) that even sometimes exceeded the Nernst limit (59 mV/pH) by means of electrostatic gating of H(+) ions. This feature was attributed to the defect-mediated chemisorptions of H(+) ions to the graphene edge, as supported by Raman measurements and observed cycling characteristics of the GM FETs. Although the H(+) ion binding to the defects increased the device response to pH change, this binding was found to be irreversible. However, the irreversible component showed relatively fast decay, almost disappearing after 5 cycles of exposure to solutions of decreasing pH value from 8.25 to 6.55. Similar behavior could be found in the Gr-FET, but the irreversible component of the response was much smaller. Finally, after complete passivation of the defects, both Gr-FETs and GM-FETs exhibited only reversible response to pH change, with similar magnitude in the range of 6-8 mV/pH.
We report the role of defects in enzymatic graphene field-effect transistor sensors by introducing engineered defects in graphene channels. Compared with conventional graphene sensors (Gr sensors), graphene mesh sensors (GM sensors), with an array of circular holes, initially exhibited a higher irreversible response to glucose, involving strong chemisorption to edge defects. However, after immobilization of glucose oxidase, the irreversibility of the responses was substantially diminished, without any reduction in the sensitivity of the GM sensors (i.e., -0.53 mV/mM for the GM sensor vs -0.37 mV/mM for Gr sensor). Furthermore, multiple cycle operation led to rapid sensing and improved the reversibility of GM sensors. In addition, control tests with sensors containing a linker showed that sensitivity was increased in Gr sensors but decreased in GM sensors. Our findings indicate that edge defects can be used to replace linkers for immobilization of glucose oxidase and improve charge transfer across glucose oxidase-graphene interfaces.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.