No abstract

The utilisation of industrial residual products to develop new value-added materials and reduce their environmental footprint is one of the critical challenges of science and industry. Development of new multifunctional and bio-based composite materials is an excellent opportunity for the effective utilisation of residual industrial products and a right step in the Green Deal's direction as approved by the European Commission. Keeping the various issues in mind, we describe the manufacturing and characterisation of the three-component bio-based composites in this work. The key components are a bio-based binder made of peat, devulcanised crumb rubber (DCR) from used tyres, and part of the fly ash, i.e., the cenosphere (CS). The three-phase composites were prepared in the form of a block to investigate their mechanical properties and density, and in the form of granules for the determination of the sorption of water and oil products. We also investigated the properties’ dependence on the DCR and CS fraction. It was found that the maximum compression strength (in block form) observed for the composition without CS and DCR addition was 79.3 MPa, while the second-highest value of compression strength was 11.2 MPa for the composition with 27.3 wt.% of CS. For compositions with a bio-binder content from 17.4 to 55.8 wt.%, and with DCR contents ranging from 11.0 to 62.0 wt.%, the compressive strength was in the range from 1.1 to 2.0 MPa. Liquid-sorption analysis (water and diesel) showed that the maximum saturation of liquids, in both cases, was set after 35 min and ranged from 1.05 to 1.4 g·g -1 for water, and 0.77 to 1.25 g·g-1 for diesel. It was observed that 90% of the maximum saturation with diesel fuel came after 10 min and for water after 35 min.

Various metals and semiconductors containing printed circuit boards (PCBs) are abundant in any electronic device equipped with controlling and computing features. These devices inevitably constitute e-waste after the end of service life. The typical construction of PCBs includes mechanically and chemically resistive materials, which significantly reduce the reaction rate or even avoid accessing chemical reagents (dissolvents) to target metals. Additionally, the presence of relatively reactive polymers and compounds from PCBs requires high energy consumption and reactive supply due to the formation of undesirable and sometimes environmentally hazardous reaction products. Preliminarily milling PCBs into powder is a promising method for increasing the reaction rate and avoiding liquid and gaseous emissions. Unfortunately, current state-of-the-art milling methods also lead to the presence of significantly more reactive polymers still adhered to milled target metal particles. This paper aims to find a novel and double-step disintegration–milling approach that can provide the formation of metal-rich particle size fractions. The morphology, particle fraction sizes, bulk density, and metal content in produced particles were measured and compared. Research results show the highest bulk density (up to 6.8 g·cm−3) and total metal content (up to 95.2 wt.%) in finest sieved fractions after the one-step milling of PCBs. Therefore, about half of the tested metallic element concentrations are higher in the one-step milled specimen and with lower adhered plastics concentrations than in double-step milled samples.

No abstract

No abstract