No abstract

In latest years, various techniques and chemicals have been used for the control of microbial influenced corrosion (MIC) of metals. The application of botanicalbased biocides is one of the effective and practical techniques in the fight against MIC. In the present study, the role of aqueous extract of ginger (Zingiber officinale) (GIE) as green biocide to control MIC of mild steel 1010 (MS) in a cooling water system was investigated. Biocorrosion behavior of Bacillus thuringiensis EN2 on MS and its control by GIE was analyzed by electrochemical measurements. Polarization, electrochemical studies (ES), weight loss measurements (WL), and surface analysis (XRD, X-ray diffraction spectroscopy, and FTIR, Fourier transform infra-red spectroscopy) were performed under various incubation periods up to 4 weeks. We observed that EN2 forms a thick biofilm on the MS metal surface at the end of the incubation period and the WL significantly increased to 993 mg at fourth week when compared to the initial immersion period (194 ± 2 mg). In contrast, with addition of GIE, WL was reduced about 41 ± 2 mg over biotic system (993 ± 2 mg). GC-MS analysis confirmed the adsorption of active component of GIE (b-turmerone) on the metal surface as a protective layer to prevent the biofilm formation and thus leads to reduction of corrosion. The optimum 20 ppm of GIE was found to be effective corrosion inhibition efficiency which was about 80%. From the results of WL, ES, XRD, FTIR, and GC-MS, GIE was identified as biocide and thus inhibits the bacterial growth on MS metal surface and it leads to control MIC. XRD showed that the GIE with EN2 resulted in less formation of corrosion products over biotic and abiotic systems. Overall, this research first shed light on the antibacterial activity of GIE inhibiting biofilm formation, thus reducing the corrosion of MS in cooling water systems.

No abstract

Silver nanoparticle-aided enhancement in the anti-corrosion potential and stability of plant extract as ecologically benign alternative for microbially induced corrosion treatment is demonstrated. Bioengineered silver nanoparticles (AgNPs) surface functionalized with plant extract material (proteinacious) was generated in vitro in a test tube by treating ionic AgNO with the leaf extract of Azadirachta indica that acted as dual reducing as well as stabilizing agent. Purity and crystallinity of the AgNPs, along with physical and surface characterizations, were evaluated by performing transmission electron microscopy, Fourier transform infrared spectroscopy, energy dispersive x-ray spectra, single-area electron diffractions, zeta potential, and dynamic light scattering measurements. Anti-corrosion studies against mild steel (MS1010) by corrosion-inducive bacterium, Bacillus thuringiensis EN2 isolated from cooling towers, were evaluated by performing electrochemical impedance spectroscopy (EIS), weight loss analysis, and surface analysis by infrared spectroscopy. Our studies revealed that AgNPs profoundly inhibited the biofilm on MS1010 surface and reduced the corrosion rates with the CR of 0.5 mm/y and an inhibition efficiency of 77% when compared to plant extract alone with a CR of 2.2 mm/y and an inhibition efficiency of 52%. Further surface analysis by infrared spectra revealed that AgNPs formed a protective layer of self-assembled film on the surface of MS1010. Additionally, EIS and surface analysis revealed that the AgNPs have inhibited the bacterial biofilm and reduced the pit on MS1010. This is the first report disclosing the application of bioengineered AgNP formulations as potent anti-corrosive inhibitor upon forming a protective layer over mild steel in cooling water towers. Graphical Abstract ᅟ.

Thermophilic bacterial communities generate thick biofilm on carbon steel API 5LX and produce extracellular metabolic products to accelerate the corrosion process in oil reservoirs. In the present study, nine thermophilic biocorrosive bacterial strains belonging to Bacillus and Geobacillus were isolated from the crude oil and produced water sample, and identified using 16S rRNA gene sequencing. The biodegradation efficiency of hydrocarbons was found to be high in the presence of bacterial isolates MN6 (82%), IR4 (94%) and IR2 (87%). During the biodegradation process, induction of the catabolic enzymes such as alkane hydroxylase, alcohol dehydrogenase and lipase were also examined in these isolates. Among them, the highest activity of alkane hydroxylase (130 µmol mg −1 protein) in IR4, alcohol dehydrogenase (70 µmol mg −1 protein) in IR2, and higher lipase activity in IR4 (60 µmol mg −1 protein) was observed. Electrochemical impedance spectroscopy and X-ray diffraction data showed that these isolates oxidize iron into ferrous/ferric oxides as the corrosion products on the carbon steel surface, whilst the crude oil hydrocarbon served as a sole carbon source for bacterial growth and development in such extreme environments.