This article investigates the toughness of yttria-stabilized zirconia (YSZ) with the tetragonal-prime ( t ′) structure. Such materials are used as durable thermal barriers in gas turbines. Their durability has been attributed to high toughness, relative to materials in the cubic phase field. Based on prior literature, a ferroelastic toughening mechanism is hypothesized and this assertion is examined by characterizing the material in the wake of an indentation-induced crack. Assessment by transmission electron microscopy, Raman spectroscopy and optical interferometry has affirmed the existence of a process zone, approximately 3 μm in width, containing a high density of nano-scale domains, with equal proportions of all three crystallographic variants. Outside the zone, individual grains contain a single variant (no domains) implying that the toughening mechanism is controlled by domain nucleation (rather than the motion of pre-existing twin boundaries). The viability of the ferroelastic toughening mechanism is assessed using a process zone model that relates the observed toughening to the stress/strain hysteresis accompanying domain formation. Based on the measured process zone size, the known tetragonality of t ′-7 wt% YSZ and the enhancement in toughness relative to cubic YSZ, consistency between the model and the observed toughening is demonstrated for a reasonable choice of the coercive stress.

No abstract

No abstract

No abstract

The polar surfaces of wurtzite-type zinc oxide (ZnO) were characterized by x-ray photoemission spectroscopy to identify the origin of the polarity dependence of the valence band spectra. A characteristic sub-peak always appeared in the valence band spectra of the (0001) face regardless of the surface preparation conditions. It also appeared in the valence band spectra of the (101¯2) face, but only when the photoelectron take-off angle was parallel to the c-axis of ZnO. Our analysis demonstrates that this take-off angle dependency originates not from the surface state, photoelectron diffraction, or the presence of surfactants but from the crystal polarity.