No abstract

Three-dimensional (3D) printing is increasingly being utilized in the dental field. After fabricating a prosthesis using a 3D printed resin, a post-curing process is required to improve its mechanical properties, but there has been insufficient research on the optimal post-curing conditions. We used various 3D printed crown and bridge materials in this study, and evaluated the changes in their properties according to post-curing time by evaluating the flexural strength, Weibull modulus, Vickers hardness, color change, degree of conversion, and biocompatibility. The obtained results confirmed that the strength of the 3D printed resin increased when it was post-cured for 60–90 min. The Vickers hardness, the degree of conversion, and biocompatibility of the 3D printed resins increased significantly around the beginning of the post-curing time, and then increased more gradually as the post-curing time increased further. It was observed that the color tone also changed as the post-curing time increased, with some groups showing a ΔE00 value of ≥ 2.25, which can be recognized clinically. This study has confirmed that, after the printing process of a 3D printed resin was completed, a sufficient post-curing time of at least 60 min is required to improve the overall clinical performance of the produced material.

Objective This study investigated the marginal and internal adaptation of individual dental crowns fabricated using a CAD/CAM system (Sirona’s BlueCam), also evaluating the effect of the software version used, and the specific parameter settings in the adaptation of crowns.Material and Methods Forty digital impressions of a master model previously prepared were acquired using an intraoral scanner and divided into four groups based on the software version and on the spacer settings used. The versions 3.8 and 4.2 of the software were used, and the spacer parameter was set at either 40 μm or 80 μm. The marginal and internal fit of the crowns were measured using the replica technique, which uses a low viscosity silicone material that simulates the thickness of the cement layer. The data were analyzed using a Friedman two-way analysis of variance (ANOVA) and paired t-tests with significance level set at p<0.05.Results The two-way ANOVA analysis showed the software version (p<0.05) and the spacer parameter (p<0.05) significantly affected the crown adaptation. The crowns designed with the version 4.2 of the software showed a better fit than those designed with the version 3.8, particularly in the axial wall and in the inner margin. The spacer parameter was more accurately represented in the version 4.2 of the software than in the version 3.8. In addition, the use of the version 4.2 of the software combined with the spacer parameter set at 80 μm showed the least variation. On the other hand, the outer margin was not affected by the variables.Conclusion Compared to the version 3.8 of the software, the version 4.2 can be recommended for the fabrication of well-fitting crown restorations, and for the appropriate regulation of the spacer parameter.

This study describes the successful synthesis of nitric oxide (NO)-releasing compounds with biodegradable and injectable properties and demonstrates that the kinetics of NO release vary according to the type of NO donor. The antimicrobial activity of NO-releasing compounds against three common periodontal pathogens, i.e., Aggregatibacter actinomycetemcomitans, Porphyromonas gingivalis, and Actinomyces israelii, was investigated using a susceptibility assay. Human gingival fibroblasts were treated with NO-releasing compounds at the minimum concentrations required for bacterial growth and cytotoxicity was evaluated using the MTT cell proliferation assay. Our results suggest that NO-releasing compounds can be used topically to treat both gram-negative and gram-positive periodontal pathogens. Comparison of the antimicrobial activity and cytotoxicity assay results between the NO-releasing compounds revealed that an NO donor comprising a macromolecule without surface charge, a lower instantaneous NO concentration, and an adequate supply of NO were associated with a strong bactericidal effect and low cytotoxicity. NO-releasing compounds with these properties may be suitable for treatment of periodontitis.