Crease cracking can be detrimental to the functionality and appearance of paperboard-based pack-aging. The effect of creasing severity on the degree of reverse-side crease cracking (bead-side of the crease) of paperboard was investigated. Samples were creased with a range of rule and channel geometries, and the cracking degree was quantified as the percent of cracked length relative to the total length of the crease. The cracking degree was typically below 5% at low crease penetration depths, but was exponentially higher beyond a critical penetration depth. A rule and channel combination with a wider clearance shifted the critical depth to larger values. The creasing severity parameter, termed the creasing draw, converged the cracking degree data from different rule and channel combinations to a single curve. The creasing draw was derived from the same analytical expres-sions as the transverse shear strain and quantifies the length of paper that is drawn into the channel during creasing. The critical draw is defined as the draw at which cracking becomes greater than 5%, which corresponds with the point at which cracking becomes exponential. The critical draw is a material/system parameter that defines the level below which cracking is minimal.

A laboratory study was conducted looking at the effects of moisture content on wet tear strength in handsheets. Three different wetting techniques were used to generate the wet tear (Elmendorf-type) data at varying moisture levels, from TAPPI standard conditions (dry) to over 60% moisture content (saturated). Unbleached hard-wood and softwood fiber from full-scale kraft pulp production were used. The softwood fiber was refined using a Valley beater to reduce freeness. Handsheets were made with a blend of hardwood and softwood and with refined softwood, without the addition of wet-end chemistry. The resulting grams-force tear data obtained from the test was indexed with basis weight and plotted versus both moisture content and dryness. As moisture content levels in the handsheets increased, the wet tear strength also increased, reaching a critical maximum point. This marked a transition point on the graph where, beyond a critical moisture content level, the tear strength began to decline linearly as moisture increased. This pattern was repeated in handsheets made from a blend of hardwood and softwood and from 100% refined softwood.

In this study, Wedge statistical analysis tools were used to collect, collate, clean up, plot, and analyze several years of operational data from a commercial paper machine. The z-direction tensile (ZDT) and Scott Bond tests were chosen as representative of fiber bond strength. After analyzing thousands of operational parameters, the ones with the most significant impact upon ZDT involved starch application method, starch penetration, and the amount of starch applied. Scott bond was found to be significantly impacted by formation and refining. Final calendering of the paper web has also shown an impact on internal fiber bonding.