Crease cracking can be detrimental to the functionality and appearance of paperboard-based pack-aging. The effect of creasing severity on the degree of reverse-side crease cracking (bead-side of the crease) of paperboard was investigated. Samples were creased with a range of rule and channel geometries, and the cracking degree was quantified as the percent of cracked length relative to the total length of the crease. The cracking degree was typically below 5% at low crease penetration depths, but was exponentially higher beyond a critical penetration depth. A rule and channel combination with a wider clearance shifted the critical depth to larger values. The creasing severity parameter, termed the creasing draw, converged the cracking degree data from different rule and channel combinations to a single curve. The creasing draw was derived from the same analytical expres-sions as the transverse shear strain and quantifies the length of paper that is drawn into the channel during creasing. The critical draw is defined as the draw at which cracking becomes greater than 5%, which corresponds with the point at which cracking becomes exponential. The critical draw is a material/system parameter that defines the level below which cracking is minimal.

Crease cracking of paperboard is important to control for the appearance and structural integrity of packages. Crease cracking is affected by creasing operation variables, as well as the physical properties of the paperboard. However, the effects of the physical properties are not clearly known. The objectives of this work were to identify the key material properties that affect crease cracking and to clarify the effects of fiber composition and starch. Laboratory sheets were produced from bleached and refined softwood and hardwood commercial pulp at grammage and thicknesses that match a typical paperboard. To mimic papermaking operations, surface starch was applied via a bench-top size press. The sheets were creased in the lab over a range of penetration depths, and reverse-side cracking was measured. The results showed that less reverse-side cracking was correlated with higher tensile post-peak energy, a lower bending stress, and a lower z-direction (ZD) stiffness. The tensile post-peak energy is a measure of the resistance to crack growth via fiber-bridging. The bending force and the ZD stiffness influence the forces that create cracks. It was observed that decreasing the ratio of hard-wood-to-softwood content and reducing the amount of starch would both decrease crease cracking.