No abstract

The purpose of this in vitro study was to evaluate the effect of different surface treatments on the shear bond strength of a resin-based cement to porcelain. Sixty pairs of 50% aluminous porcelain discs were fabricated. In each pair, one disc measured 6 mm in diameter X 3 mm thickness (A) and the other measured 3 mm in diameter X 3mm thickness (B). The specimens were randomly assigned to 6 groups (n=10 pairs of discs), according to the surface treatment: etching with 10% hydrofluoric acid for 2 or 4min (G1 and G2); 50-μm particle aluminum oxide sandblasting for 5 s (G3); sandblasting followed by etching for 2 or 4min (G4 and G5) and control -no treatment (G6). A silane agent was applied to the treated surface of both discs of each pair. Bistite II DC dual-cure resin cement was applied and the B discs were bonded to their respective A discs. Specimens were stored in distilled water at 37ºC for 24 h and were tested in shear strength at a crosshead speed of 2 mm/min. Means in MPa were: G1: 14.21 ± 4.68; G2: 8.92 ± 3.02; G3: 10.04 ± 2.37; G4: 12.74 ± 5.15; G5: 10.99 ± 3.35; G6: 6.09 ± 1.84. Data were compared by one-way ANOVA and Tukey's test at 5% significance level. Bond strength recorded after 2-min acid etching was significantly higher than 4-min etching (p<0.05) and control (p<0.05), but did not differ significantlyfrom sandblasting alone (p>0.05) or followed by etching for 2 or 4 min (p>0.05). Within the limitations of an in vitro study, it may be concluded that 2-min hydrofluoric acid etching produced a favorable micromechanical retention that enhanced resin cement bond strength to porcelain.

RESUMOObjetivo: Avaliar, in vitro a micromorfologia da interface da união sistema restaurador-dentina decídua, em função do sistema adesivo e do instrumento cortante rotatório. Método: Foram utilizados 20 segundos molares decíduos divididos aleatoriamente em dois grupos (n=10). No grupo C, foi realizado desgaste, até atingir a dentina, com ponta carbide. No grupo D, foi feito o mesmo desgaste, porém com ponta diamantada. A superfície preparada de cada dente foi dividida ao meio, sendo que em uma metade foi aplicado um sistema adesivo convencional de duas etapas (Single-Bond -3M) e na outra um sistema autocondicionante de etapa única (One Up Bond F -Tokuyama). Todos os dentes foram restaurados com a resina composta híbrida (Filtek Z250 -3M). As amostras foram termocicladas, embutidas em resina, seccionadas para obtenção da interface de união e preparadas para observação ao MEV. Resultados: Os dois sistemas adesivos utilizados foram capazes de formar camada híbrida. O sistema adesivo convencional de duas etapas proporcionou melhor selamento da interface de união, quando comparada ao autocondicionante e o emprego da ponta diamantada com o adesivo autocondicionante, mostrou o pior selamento da interface de união, com os maiores valores de gap. Conclusão: O instrumento cortante rotatório (ponta diamantada) só apresentou influência negativa na qualidade da interface sistema restaurador-dentina decídua quando se empregou sistema adesivo autocondicionante de etapa única. DESCRIPTORS DESCRITORESInstrumentos odontológicos; Adesivos dentinários; Dente decíduo. Purpose:To evaluate, in vitro, the micromorphology of the restorative system-primary dentin interface as a function of the adhesive system and rotary cutting instrument. Method: Twenty primary second molars were randomly assigned to two groups (n=10). In group C, the teeth were ground with a carbide bur until reaching the dentin. In group D, the same procedure was done however using a diamond bur. The prepared surface of each tooth was bisected. In one half, a 2-step total-etch adhesive system (Single-Bond -3M) was applied and in the other half, a 1-step self-etching adhesive system (One Up Bond F -Tokuyama) was applied. All teeth were restored with a hybrid composite resin (Filtek Z250 -3M). The specimens were thermocycled, embedded in resin, sectioned to obtain the adhesive interface and prepared for SEM analysis. Results: Both adhesive systems were capable of forming a hybrid layer. The 2-step total-etch adhesive system provided a better sealing of the adhesive interface, in comparison to the self-etching adhesive system. The use of a diamond bur together with the selfetching adhesive system yielded the worst sealing of the adhesive interface, with presence of larger gaps. Conclusions: The rotary cutting instrument (diamond bur) had a negative influence on the quality of the restorative system-primary dentin interface only when a 1-step self-etching adhesive system was used.Dental instruments; Adhesive system; Deciduous tooth.

O objetivo deste estudo foi investigar in vitro o comportamento das facetas de Artglass e Targis quando submetidas à inserção e remoção de grampos circunferenciais de cromocobalto. Foram confeccionadas 24 coroas veneer (12 com facetas de Artglass e 12 com Targis), bem como os respectivos grampos circunferenciais em cromo-cobalto. Utilizando um dispositivo elaborado para este fim, as coroas foram submetidas a cinco mil ciclos de inserção e remoção dos grampos. Para avaliar os efeitos dos ciclos sobre os corpos-de-prova, foram utilizadas a verificação da força necessária para remover os grampos das coroas e a inspeção macroscópica das coroas. A força necessária para remoção dos grampos das coroas não foi alterada significativamente durante o experimento. Entretanto, todas as coroas apresentaram uma área de abrasão, observável por inspeção visual. Deste modo, é possível depreender que as facetas feitas com Artglass e Targis sofrem abrasão decorrente da inserção e remoção de grampos circunferenciais em cromo-cobalto, mas esta abrasão não influenciou significativamente a força necessária para remover o grampo da coroa durante este estudo.