Large-scale transparent and flexible electronic devices have been pursued for potential applications such as those in touch sensors and display technologies. These applications require that the power source of these devices must also comply with transparent and flexible features. Here we present transparent and flexible supercapacitors assembled from polyaniline (PANI)/single-walled carbon nanotube (SWNT) composite thin film electrodes. The ultrathin, optically homogeneous and transparent, electrically conducting films of the PANI/SWNT composite show a large specific capacitance due to combined double-layer capacitance and pseudo-capacitance mechanisms. A supercapacitor assembled using electrodes with a SWNT density of 10.0 µg cm(-2) and 59 wt% PANI gives a specific capacitance of 55.0 F g(-1) at a current density of 2.6 A g(-1), showing its possibility for transparent and flexible energy storage.

We report the synthesis of ultrafine S nanoparticles with diameter 10 ~ 20 nm via a membrane-assisted precipitation technique. The S nanoparticles were then coated with conducting poly (3,4-ethylenedioxythiophene) (PEDOT) to form S/PEDOT core/shell nanoparticles. The ultrasmall size of S nanoparticles facilitates the electrical conduction and improves sulfur utilization. The encapsulation of conducting PEDOT shell restricts the polysulfides diffusion, alleviates self-discharging and the shuttle effect, and thus enhances the cycling stability. The resulting S/PEDOT core/shell nanoparticles show initial discharge capacity of 1117 mAh g−1 and a stable capacity of 930 mAh g−1 after 50 cycles.

Catalysts for oxygen reduction reaction (ORR) are at the heart of key green-energy fuel cell technology. N-doped graphene is a potential metal-free electrode with much better electrocatalytic activity, long-term stability, and tolerance to crossover effect than expensive platinum-based electrocatalysts. Here, we report a feasible direct-synthesis method in preparing N-graphene with manageable N contents in a large scale. The resultant N-graphene used as electrocatalysts exhibits similar catalytic activity but superior stability compared to commercial Pt/C for ORR in an alkaline solution. It was found that their electrocatalytic activities were demonstrated to depend largely on N-doping content. When nitrogen content reaches a high value at about 24–25%, ORR reaction exhibits a favorable formation of water via a four-electron pathway. Furthermore, the effect of pyrolysis temperature and precursor on the activity of N-graphene is systematically analyzed, and may shed some light on the principle of choosing appropriate way for preparing N-graphene.