This study aimed to evaluate the effect of silver diamine fluoride (SDF) and potassium iodide (KI) on the formation of cariogenic biofilm and surface roughness in vitro. A total of 48 bovine dentin specimens with artificially induced caries were prepared and divided into 3 groups of 16: untreated control, SDF-treated, and SDF-treated followed by KI (SDFKI). Ten specimens from each group were used to observe microbial adhesion. Multispecies cariogenic biofilms including Streptococcus mutans , Lactobacillus casei , and Candida albicans were cultured on the specimens. Microbes were cultured for 24 hours, and the colony-forming unit was calculated. The remaining specimens were observed by atomic force microscope and scanning electron microscope (SEM). The number of bacteria was significantly lower in the SDF and SDFKI groups. KI did not inhibit the antibacterial activity of SDF significantly. SEM images showed particles generated after SDF and SDFKI application were deposited on the dentin, but there was no significant difference in surface roughness between the 3 groups. This study confirmed that SDF and SDFKI application did not have a significant effect on the surface roughness of dentin, but effectively inhibited the formation of the early cariogenic bacterial film after 24 hours compared to the control.

Restoring composite resins with the optimal shades for all primary teeth is a great challenge for pediatric dentists. A newly developed single-shade composite resin can exhibit a color similar to that of the surrounding tooth structure based on the structural color phenomenon. This study aims to evaluate the color adjustment potential (CAP) of a single-shade composite resin compared to conventional multi-shade composite resins in primary teeth. A single-shade composite resin and two conventional multi-shade composite resins were included in this study. Two types of specimens, a single specimen and a dual specimen, were evaluated. For single specimens, duplications of the primary second molar denture teeth were made using experimental composite resins. For dual specimens, cavities were prepared on the buccal surfaces of extracted primary second molars and restored with experimental composite resins. The L*, a*, and b* values were measured using a colorimeter for the extracted teeth and specimens. The mean ΔE_ab^* values for single and dual specimens and CAP were calculated. Bonferroni post-hoc analysis was performed to confirm the statistical significance between the ΔE_ab^* and CAP values of the experimental resins. Among the single specimens, the single-shade composite resin showed significantly higher ΔE_Single compared to other composite resins (<i>p</i> < 0.0167). There was no significant difference between ΔE_Dual for all experimental resins. The single-shade composite resin showed highest CAP compared to other multi-shade composite resins. A single-shade composite resin exhibited the most prominent color adaptability compared to other conventional multi-shade composite resins for primary second molars. A single-shade composite resin can simplify shade matching and provide esthetic outcomes for the restoration of primary second molars.

This study investigated the effects of silver diamine fluoride (SDF) and potassium iodide (KI) treatments on the acid resistance of dentin exposed to secondary caries. Sixteen bovine dentin specimens with artificially induced caries were assigned to the following four groups: untreated negative control, untreated positive control, SDF-treated (SDF), and SDF and KI-treated (SDFKI). Multispecies cariogenic biofilms containing <i>Streptococcus mutans</i>, <i>Lactobacillus casei</i>, and <i>Candida albicans</i> were cultured on the specimens for 28 days, except for the negative control group. Specimens from the negative control group were stored in phosphate-buffered saline for that period. After a cariogenic biofilm challenge, the degree of demineralization was evaluated using micro-computed tomography (micro-CT). As a result of data analysis using micro-CT, the demineralization depths of the negative control, positive control, SDF, and SDFKI groups were 149.0 ± 7 μm, 392.0 ± 11 μm, 206.0 ± 20 μm, and 230.0 ± 31 μm, respectively. The degree of demineralization was significantly reduced in the SDF and SDFKI groups compared with that in the untreated positive control group. There were no significant differences between the SDF and SDFKI groups. This study confirmed that SDF and SDFKI treatments increase the acid resistance of dentin to secondary caries. KI did not significantly affect the cariesarresting effect of the SDF.

This study compared the surface roughness and microbial adhesion characteristics of Omnichroma, a novel composite resin developed using “smart chromatic technology”, with those of two other conventional composite resins with different filler compositions. A total of 144 specimens were fabricated using 3 types of composite resins: Omnichroma (nano-spherical), Filtek Z350XT (nanofill), and Tetric N-Ceram (nanohybrid) and, divided into 3 groups of 48. Finishing was performed using tungsten carbide burs. Specimens were then divided into 3 subgroups using different polishing methods: Control, SofLex, and PoGo. Surface roughness was analyzed quantitatively and qualitatively using an atomic force microscope and a scanning electron microscope. Microbial adhesion was assessed by culturing <i>Streptococcus mutans</i> on the specimens for 24 hours and then measuring colony-forming units attached to the upper surface. The surface roughness (Ra) of Omnichroma was 0.123 μm after finishing, and it exhibited a smooth surface compared to the other resins. However, after polishing, there were no significant differences in the surface roughness between the three composite groups, regardless of the polishing methods. The surfaces of the Control subgroups were significantly rougher than those of the SofLex subgroups in all 3 composite groups. However, except for Tetric N-Ceram, there were no significant differences between the Control and PoGo subgroups in the other composite groups. Microbial adhesion assessment showed no significant differences between any of the 3 composite resin subgroups; however, Omnichroma exhibited higher microbial adhesion than the other two composites. No significant correlation was observed between surface roughness and microbial adhesion.

Distal displacement of the tooth germ of the mandibular second premolar (MnP2) leads to its impaction and obturation of the eruption path of the mandibular first molar delaying its eruption. The present case report describes the treatment of 2 cases of eruption guidance for distally displaced developing MnP2 that caused delayed eruption of the mandibular first molar. Intentional extraction of primary predecessor results in the mesial shift of the displaced MnP2. However, unfavorable distal ectopic eruption of the mandibular first premolar after the premature loss of primary second molar has been previously reported. Hemisection and sequential extraction of the mandibular primary second molar were performed to mesially shift the distally displaced MnP2, while preventing unfavorable distal ectopic eruption of the mandibular first premolar.