No abstract

No abstract

We investigated the potential of a nanofiber-based poly(DL-lactide-co-glycolide) (PLGA) scaffold to be used for cartilage reconstruction. The mechanical properties of the nanofiber scaffold, degradation of the scaffold and cellular responses to the scaffold under mechanical stimulation were studied. Three different types of scaffold (lactic acid/glycolic acid content ratio = 75 : 25, 50 : 50, or a blend of 75 : 25 and 50 : 50) were tested. The tensile modulus, ultimate tensile stress and corresponding strain of the scaffolds were similar to those of skin and were slightly lower than those of human cartilage. This suggested that the nanofiber scaffold was sufficiently mechanically stable to withstand implantation and to support regenerated cartilage. The 50 : 50 PLGA scaffold was degraded faster than 75 : 25 PLGA, probably due to the higher hydrophilic glycolic acid content in the former. The nanofiber scaffold was degraded faster than a block-type scaffold that had a similar molecular weight. Therefore, degradation of the scaffold depended on the lactic acid/glycolic acid content ratio and might be controlled by mixing ratio of blend PLGA. Cellular responses were evaluated by examining toxicity, cell proliferation and extracellular matrix (ECM) formation using freshly isolated chondrocytes from porcine articular cartilage. The scaffolds were non-toxic, and cell proliferation and ECM formation in nanofiber scaffolds were superior to those in membrane-type scaffolds. Intermittent hydrostatic pressure applied to cell-seeded nanofiber scaffolds increased chondrocyte proliferation and ECM formation. In conclusion, our nanofiber-based PLGA scaffold has the potential to be used for cartilage reconstruction.

No abstract

Magnesium calcium phosphate biocement (MCPB) with rapid-setting characteristics was fabricated by using the mixed powders of magnesium oxide (MgO) and calcium dihydrogen phosphate (Ca(H 2 PO 4 ) 2 . H 2 O). The results revealed that the MCPB hardened after mixing the powders with water for about 7 min, and the compressive strength reached 43 MPa after setting for 1 h, indicating that the MCPB had a short setting time and high initial mechanical strength. After the acid -base reaction of MCPB containing MgO and Ca(H 2 PO 4 ) 2 . H 2 O in a molar ratio of 2 : 1, the final hydrated products were Mg 3 (PO 4 ) 2 and Ca 3 (PO 4 ) 2 . The MCPB was degradable in Tris-HCl solution and the degradation ratio was obviously higher than calcium phosphate biocement (CPB) because of its fast dissolution. The attachment and proliferation of the MG 63 cells on the MCPB were significantly enhanced in comparison with CPB, and the alkaline phosphatase activity of MG 63 cells on the MCPB was significantly higher than on the CPB at 7 and 14 days. The MG 63 cells with normal phenotype spread well on the MCPB surfaces, and were attached in close proximity to the substrate, as seen by scanning electron microscopy (SEM). The results demonstrated that the MCPB had a good ability to support cell attachment, proliferation and differentiation, and exhibited good cytocompatibility.