ABSTRAKPenelitian ini diawali dengan pembuatan fotokatalis TiO2-Cu dengan cara impregnasi basah dan fotodeposisi, pada perbandingan mol TiO2 : Cu 2+ adalah 100:0 ; 99:1 ; 98:2 ; 97:3 dan 96:4. Fotokatalis dikarakterisasi menggunakan SEM, UV-Vis DRS, FTIR dan XRD. Hasil karakterisasi menunjukkan telah berhasil dilakukan sintesis TiO2-Cu. Dari karakterisasi SEM terlihat bahwa penambahan logam Cu akan merubah morfologi dari fotokatalis TiO2. Berdasarkan analisis UV-Vis DRS, penambahan dopan logam Cu menurunkan energi celah pita dari TiO2. Dari analisis XRD muncul nilai 2θ pada 29,607 dan 48,401 yang menunjukkan terbentuknya kristal monoclinic H2Ti3O7. Hasil analisis FTIR menunjukkan terjadinya perubahan serapan spesifik dari TiO2 yang menandakan terjadi perubahan struktur dari TiO2.Kata Kunci: Fotokatalis, Karakterisasi, Sintesis, TiO2-Cu ABSTRACTThis study begins with the manufacture of TiO2 -Cu photocatalyst by means of wet impregnation and fotodeposisi, the mole ratio of TiO2: Cu 2+ is 100: 0; 99: 1; 98: 2; 97: 3 and 96: 4. Photocatalysts were characterized using SEM, UV-Vis DRS, FTIR and XRD. The results showed has been successfully carried out the synthesis of TiO2-Cu. From SEM characterization shows that the addition of Cu metal will alter the morphology of TiO2 photocatalysts. Based on analysis of UV-Vis DRS, the addition of Cu metal dopant to decrease the energy band gap of TiO2. From XRD analysis appears 2θ value at 29.607 and 48.401 which indicates the formation of monoclinic crystal H2Ti3O7. FTIR analysis results indicate a change in the specific uptake of TiO2 indicating a change in the structure of TiO2. Keywords: Characterization, Photocatalyst, Synthesis, TiO2-Cu PENDAHULUANTitanium dioksida adalah bahan semikonduktor yang telah banyak digunakan pada berbagai aplikasi; antara lain sel surya, fotokatalis, sensor biologis dan kimia, produk kesehatan hingga pigmentasi cat. TiO2 menjadi pilihan dalam banyak aplikasi fotokimia dan fitoelektrokimia karena biaya pembuatannya relatif murah, tersedia luas dan tidak beracun. Teknologi fotokatalisis merupakan kombinasi dari proses fotokimia dan katalis yang terintegrasi untuk dapat melangsungkan suatu reaksi transformasi kimia. Titanium dioksida menyerap cahaya yang memiliki tingkat energi lebih tinggi dibanding tingkat energi celah pitanya menyebabkan elektron melompat ke pita konduksi dan meninggalkan hole di pita valensi. Kristal rutil memiliki energi celah pita 3,0 eV dananatase memiliki energi celah pita 3,2 eV sehingga keduanya akan menyerap sinar ultraviolet.Pemanfaatan fotokatalis saat ini dikembangkan untuk mendapatkan

Studi penggunaan fotokatalis TiO2/KA (arang aktif) dilakukan dengan tujuan mengurangi konsentrasi zat warna pada limbah cair tekstil. Arang aktif dari jerami padi diperoleh dari Kabupaten Banyumas dan contoh dari limbah cair tekstil dari salah satu industri tekstil di Pemalang. Penelitian ini dimulai dengan pembuatan arang aktif dari jerami padi, dengan aktivasi termal pada temperatur 300 oC dan 700 oC, kemudian dilakukan modifikasi fotokatalis TiO2/KA. Uji fotodegradasi zat warna dilakukan dengan beberapa parameter seperti perbandingan berat TiO2: KA (99:1, 98:2, 97:3, 96:4, 95:5) dan pH (2, 5, 7, 9, 13). Karekterisasi fotokatalis menggunakan SEM, konsentrasi pewarna menggunakan spektrofotometri UV-Vis. Hasil penelitian menunjukkan bahwa aktivitas fotokatalis optimum dalam perbandingan berat TiO2: KA300 (99 : 1) dengan menurunkan konsentrasi zat warna adalah 49,19%, berarti sementara TiO2: KA700 (97 : 3) dengan penurun konsentrasi zat warna adalah 52,02%. Proses yang optimal untuk fotodegadasi zat warna pada pH 2 dengan penurunan konsentrasi zat warna pada TiO2: KA300 (99 : 1) adalah 83,80% dan untuk TiO2: KA700 (97:3) adalah 85,66%.

No abstract

Cyanide compound is one of the organic material contained in wastewater of tapioca production, which is a highly toxic substance for life. According to the results of physical and chemical properties of liquid waste samples of tapioca starch in the deposition process in the industry taken from Pancasan Village, Ajibarang, Banyumas, cyanide concentration in the effluent was 3.8 mg/L while the maximum level of cyanide allowed in industrial wastewater are 0.5 mg/L. Therefore, a method to reduce the concentration of cyanide is needed. One of the method is using of TiO 2 catalyst. This study was aimed to determine the effect of the pH and UV irradiation time on photocatalytic activity of TiO 2 to reduce the levels of cyanide on tapioca wastewater from PT. HARUM BUNGA, Purbalingga.This study uses a thin layer of TiO 2 photocatalyst prepared by suspension of TiO 2 coating on the glass plate that was dried at 120ºC and conducted with variations of pH that were 2, 5, 7, 8, 9, 10, and 13 in the wastewater to determine the optimum pH, continued by time variation of UV radiation for 1, 2, 4, 6, 8, 10, and 12 hours. The results showed that the largest percentage decrease in the concentration of cyanide occurs at pH 9 that is equal to 88.6361% and the largest percentage decrease in the concentration of cyanide by irradiation with UV light occurs after 10 hours irradiation, up to 93.7929%.Keyword: photocatalyst, cyanide, TiO 2 PENDAHULUANIndustri tapioka adalah salah satu industri yang berkembang pesat di Indonesia. Industri ini menghasilkan limbah padat dan cair. Limbah padat ini dapat dimanfaatkan untuk berbagai keperluan, seperti; limbah padat yang berasal dari proses pengupasan ketela pohon dari kulitnya yaitu berupa kotoran dan kulit serta pada waktu pemrosesan yang berupa ampas dimana sebagian besar berupa serat dan pati dapat dimanfaatkan sebagai makanan ternak, pupuk, bahan campuran saus, dan obat nyamuk bakar. Sedangkan Limbah cair yang dihasilkan dari proses pembuatan, baik dari pencucian bahan baku sampai pada proses pemisahan pati dari airnya dapat dimanfaatkan untuk minuman nata de cassava. Limbah industri tapioka yang mempunyai kandungan bahan organik yang tinggi, apabila tidak diolah dengan baik dan benar dapat menimbulkan berbagai masalah bagi kesehatan, misalnya: gatal-gatal, timbul bau yang tidak sedap, air limbah bila masuk ke dalam tambak akan merusak tambak sehingga ikan mati, estetika sungai berubah dan lain-lain (Wahyuadhy, 1996). Senyawa sianida adalah salah satu bahan organik yang terdapat dalam limbah tapioka yang merupakan suatu substansi yang sangat beracun bagi kehidupan makhluk hidup (Ariesyady, 1996). Sianida terdapat di alam yang secara alamiah memang ada ataupun menjadi ada karena kesengajaan dari manusia dalam memenuhi kebutuhan hidupnya. Menurut hasil pemeriksaan sifat fisika kimia contoh air limbah tapioka pada proses pengendapan pati di pabrik tapioka Desa Pancasan,

Chitosan is biopolymer obtained from chitin deacetylation reaction. Chitin is a constituent of shrimps’ outer shell. Chitosan modification using crosslinker agent could increase the active groups and stabilize the physical character. One of non-toxic crosslink agents was tripolyphosphate. This study aimed at synthesizing tripolyphosphate crosslinked chitosan (TPP-Cs) to test the antioxidant and toxicity. Synthesizing tripolyphosphate chitosan was conducted using ionic gelation method. The antioxidant activity test was studied from DPPH radicals scavenging and the ability to inhibit linoleic acid oxidation. The toxicity test was using BSLT (Brine Shrimp Lethality Test) method and Artemia salina leach nauplii. The study showed that TPP-Cs could be synthesized from pink shrimp and showed antioxidant activity. The activity was due to amino and hydroxyl groups. The BSLT method showed that TPP-Cs had the potential to be applied for antibacterial, antivirus, or anticancer products.