Vertically aligned InGaN/GaN nanorod light emitting diode (LED) arrays were created from planar LED structures using a new top-down fabrication technique consisting of a plasma etch followed by an anisotropic wet etch. The wet etch results in straight, smooth, well-faceted nanorods with controllable diameters and removes the plasma etch damage. 94% of the nanorod LEDs are dislocation-free and a reduced quantum confined Stark effect is observed due to reduced piezoelectric fields. Despite these advantages, the IQE of the nanorod LEDs measured by photoluminescence is comparable to the planar LED, perhaps due to inefficient thermal transport and enhanced nonradiative surface recombination.
Ultraviolet light emitting diodes (LEDs) have been grown using metalorganic vapor phase epitaxy, while monitoring the 550 nm reflected light intensity. During nucleation of GaN on sapphire, the transition from three-dimensional (3D) grain growth to two-dimensional (2D) coalesced growth was intentionally delayed in time by lowering the NH3 flow during the initial high temperature growth. Initially, when the reflectance signal is near zero, the GaN film is rough and composed of partly coalesced 3D grains. Eventually, the reflected light intensity recovers as the 2D morphology evolves. For 380 nm LEDs grown on 3D nucleation layers, we observe increased light output. For LEDs fabricated on GaN films with a longer recovery time an output power of 1.3 mW at 20 mA current was achieved.
Using in situ wafer-curvature measurements of thin-film stress, we determine the critical thickness for strain relaxation in AlxGa1−xN∕GaN heterostructures with 0.14⩽x⩽1. The surface morphology of selected films is examined by atomic force microscopy. Comparison of these measurements with critical-thickness models for brittle fracture and dislocation glide suggests that the onset of strain relaxation occurs by surface fracture for all compositions. Misfit-dislocations follow initial fracture, with slip-system selection occurring under the influence of composition-dependent changes in surface morphology.
Stable single-mode lasing operation from a pair of coupled GaN nanowires is demonstrated through optical pumping. GaN nanowires with different lengths were placed side-by-side in contact to form a coupled cavity through nanoprobe manipulation. Unlike individual nanowire lasers, which operate in a combined multiple transverse and multiple longitude mode oscillation, a coupled nanowire-pair provides a mode selection mechanism through the Vernier effect, which can strongly enhance the free spectrum range between adjacent resonant modes and generate a stable single-mode operation with a high side-mode suppression ratio.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.