Back Surface Field (BSF) has been used as one of means to enhance solar cell performance by reducing surface recombination velocity (SRV). One of methods to produce BSF is by introducing highly doped layer on rear surface of the wafer. Depending on the type of the dopant in wafer, the BSF layer could be either p+ or n+. This research aims to compare the performance of BSF layer both in p-type and n-type wafer in order to understand the effect of BSF on both wafer types. Monociystalline silicon wafer with thickness of 300 μm. area of 1 cm2, bulk doping level NB = 1.5×1016/cm3 both for p-type wafer and n-type wafer are used. Both wafer then converted into solar cell by adding emitter layer with concentration NE =7.5×1018/cm3 both for p-type wafer and n-type wafer. Doping profile that is used for emitter layer is following complementary error function (erfc) distribution profile. BSF concentration is varied from 1×1017/cm3 to 1×1020/cm3 for each of the cell. Solar cell performance is tested under standard condition, with AM1.5G spectrum at 1000 W/m2. Its output is measured based on its open circuit voltage (Voc). short circuit current density (JSC), efficiency (η). and fill factor (FF). The result shows that the value of VOC is relatively constant along the range of BSF concentration, which is 0.694 V – 0.702 V. The same pattern is also observed in FF value which is between 0.828 – 0.831. On the other hand, value of JSC and efficiency will drop against the increase of BSF concentration. Highest JSC which is 0.033 A/cm2 and highest efficiency which is 18.6% is achieved when BSF concentration is slightly higher than bulk doping level. The best efficiency can be produced when BSF concentration is around 1×1017cm-3.. This result confirms that surface recombination velocity has been reduced due to the increase in cell’s short circuit current density and its efficiency. In general both p-type and n-type wafer will produce higher efficiency when BSF is applied. However, the increase is larger in p-type wafer than in n-type wafer. Better performance for solar cell is achieved when BSF concentration is slightly higher that bulk doping level because at very high BSF concentration the cell’s efficiency will be decreased.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.