An amorphous InGaZnO film fabricated by radio frequency magnetron sputtering in only an Ar-reactive gas shows high conductivity, and a thin-film transistors (TFTs)-based IGZO active layer expresses a poor on/off current ratio with a high off current and high subthreshold swing (SS). This paper presents the post-annealing effects on IGZO thin films to compensate the oxygen deficiencies in films as well as on TFT devices to reduce the densities of the interface trap between the active layer and insulator. The ratio of oxygen vacancies over total of oxygen (O 2 /O tot ) in IGZO estimated by the XPS measurement shows that they significantly diminish from 24.75 to 17.68% when increasing the temperature treatment to 350 • C, which is related to the enhancement in resistivity of IGZO. The TFT characteristics of IGZO treated in air at 350 • C show a high I ON /I OFF ratio of ∼1.1 × 10 7 , a high field-effect mobility of 7.48 cm 2 V −1 s −1 , and a low SS of 0.41 V dec −1 . The objective of this paper is to achieve a successful reduction in the interface trap density, D it , which has been reduced about 3.1 × 10 12 cm −2 eV −1 and 2.0 × 10 12 cm −2 eV −1 for the 350 and 200 • C treatment samples compared with the as-deposited one. The resistivity of the IGZO films can be adjusted to the appropriate value that can be used for TFT applications by controlling the treatment temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.