We present our femtosecond optical pump-probe studies of proximized ferromagnet-superconductor nanobilayers. The weak ferromagnetic nature of a thin NiCu film makes it possible to observe the dynamics of the nonequilibrium carriers through the near-surface optical reflectivity change measurements. The subpicosecond biexponential reflectivity decay has been identified as electron-phonon Debye and acoustic phonon relaxation times, and the decay of Debye phonons versus temperature dependence was used to evaluate the electronphonon coupling constants for both the pure Nb and proximized Nb/ NiCu heterostructures down to low temperatures. We have also demonstrated that the NiCu overlay on top of Nb dramatically reduced the slow, bolometric component of the photoresponse component, making such bilayers attractive for future radiation detector applications.
We report on measurements of the switching current distributions on two-dimensional superconducting NbTiN strips that are 5 nm thick and 80 nm wide. We observe that the width of the switching current distributions has a non-monotonous temperature dependence, where it is constant at the lowest temperatures up to about 1.5 K, after which it increases with temperature until 2.2 K. Above 2.5 K any increase in temperature decreases the distribution width which at 4.0 K is smaller than half the width observed at 0.3 K. By using a careful analysis of the higher order moments of the switching distribution, we show that this temperature dependence is caused by switching due to multiple fluctuations. We also find that the onset of switching by multiple events causes the current dependence of the switching rate to develop a characteristic deviation from a pure exponential increase, that becomes more pronounced at higher temperatures, due to the inclusion of higher order terms.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.