Blood Concentrates (BCs) are autologous non-transfusional therapeutical preparations with biological properties applied in tissue regeneration. These BCs differ in the preparation method, in fibrin network architecture, growth factors release as well as in platelet/cell content. Methodological changes result in distinct matrices that can compromise their clinical effectiveness. The present study evaluated the influence of different g-forces and types of tubes in the release of vascular endothelial growth factor (VEGF) from platelet-rich fibrin (PRF) as a function of time. The PRF-like samples were obtained with three g-forces (200, 400, and 800 x g) for 10 minutes in pure glass tubes or in polystyrene-clot activator tubes. Scanning and Transmission electron microscopy was used to morphometric analyzes of PRF's specimens and flow cytometry was used to quantify VEGF slow release until 7 days. Our results showed that platelets were intact and adhered to the fibrin network, emitting pseudopods and in degranulation. The fibrin network was rough and twisted with exosomic granulations impregnated on its surface. An increase in the concentration of VEGF in the PRF supernatant was observed until 7 days for all g forces (200, 400 or 800 xg), with the highest concentrations observed with 200 x g, in both tubes, glass or plastic. Morphological analyzes showed a reduction in the diameter of the PRF fibers after 7 days. Our results showed that g-force interferes with the shape of the fibrin network in the PRF, as well as affect the release of VEGF stored into platelets. This finding may be useful in applying PRF to skin lesions, in which the rapid release of growth factors can favor the tissue repair process. Our observations point to a greater clarification on the methodological variations related to obtaining PRF matrices, as they can generate products with different characteristics and degrees of effectiveness in specific applications.

Blood Concentrates (BCs) are autologous non-transfusional therapeutical preparations with biological properties applied in tissue regeneration. These BCs differ in the preparation method, in fibrin network architecture, growth factors release as well as in platelet/cell content. Methodological changes result in distinct matrices that can compromise their clinical effectiveness. The present study evaluated the influence of different g-forces and types of tubes in the release of vascular endothelial growth factor (VEGF) from platelet-rich fibrin (PRF) as a function of time. The PRF-like samples were obtained with three g-forces (200, 400, and 800 x g) for 10 minutes in pure glass tubes or in polystyrene-clot activator tubes. Scanning and Transmission electron microscopy was used to morphometric analyzes of PRF’s specimens and flow cytometry was used to quantify VEGF slow release until 7 days. Our results showed that platelets were intact and adhered to the fibrin network, emitting pseudopods and in degranulation. The fibrin network was rough and twisted with exosomic granulations impregnated on its surface. An increase in the concentration of VEGF in the PRF supernatant was observed until 7 days for all g forces (200, 400 or 800 x g), with the highest concentrations observed with 200 x g, in both tubes, glass or plastic. Morphological analyzes showed a reduction in the diameter of the PRF fibers after 7 days. Our results showed that g-force interferes with the shape of the fibrin network in the PRF, as well as affect the release of VEGF stored into platelets. This finding may be useful in applying PRF to skin lesions, in which the rapid release of growth factors can favor the tissue repair process. Our observations point to a greater clarification on the methodological variations related to obtaining PRF matrices, as they can generate products with different characteristics and degrees of effectiveness in specific applications.

No abstract

The scaffolds and their interaction with mesenchymal stem cells are objects of study in bioengineering and tissue repair. Mechanisms such as surface adhesion, proliferation, viability, and cytotoxicity are essential for the development of therapies. The present study analyzed the influence of platelet-rich fibrin (PRF) in viability, cytotoxicity, and proliferation of stem cells from human exfoliated deciduous teeth (SHED) exposed to bovine biomaterial surfaces. The studied groups were divided and analyzed as follows: (S) only SHED as control Group; (SB) SHED + biomaterial; (SBP) SHED + biomaterial + PRF. Analyses of cells seeded in 24-well plates were performed after 24, 48 and 72 hours. Individual groups were subjected to viability, cytotoxicity and cell proliferation tests using neutral red, MTT and crystal violet, respectively; and in the 72-hour group, scanning electron microscopy (SEM) was performed to record cell ultra-morphology. Data were submitted to statistical analysis by two-factor ANOVA with a significance level of 5%. The results demonstrated a better performance in the viability/cytotoxicity and proliferation of stem cells for the group (SBP) in comparison to the group (SB) and the group (S). The applied statistical tests showed that the biomaterial factor, time, and interaction between them gave rise to results with statistical significance. SHED submitted to bovine biomaterial were more viable, proliferative and with lower toxicity when associated with PRF. PRF seemed to activate the metabolism of stem cells in culture, indicating that such an association can bring an effective benefit in clinical outcome.

No abstract