No abstract

Synthetic polymers are the cause of some major environmental impacts due to their low degradation rates. Polyurethanes (PU) are widely used synthetic polymers, and their growing use in industry has produced an increase in plastic waste. A commercial polyether-based thermoplastic PU with hydrolytic stability and fungus resistance was only attacked by an entomopathogenic fungus, Metarhiziumanisopliae, when the films were pre-treated with Ultraviolet (UV) irradiation in the presence of reactive atmospheres. Water contact angle, Fourier transform infrared spectroscopy in attenuated total reflection mode (FTIR-ATR), scanning electron microscopy (SEM), and profilometer measurements were mainly used for analysis. Permanent hydrophilic PU films were produced by the UV-assisted treatments. Pristine polyether PU films incubated for 10, 30, and 60 days did not show any indication of fungal growth. On the contrary, when using oxygen in the UV pre-treatment a layer of fungi spores covered the sample, indicating a great adherence of the microorganisms to the polymer. However, if acrylic acid vapors were used during the UV pre-treatment, a visible attack by the entomopathogenic fungi was observed. SEM and FTIR-ATR data showed clear evidence of fungal development: growth and ramifications of hyphae on the polymer surface with the increase in UV pre-treatment time and fungus incubation time. The results indicated that the simple UV surface activation process has proven to be a promising alternative for polyether PU waste management.

Environmental pollution by plastic debris is estimated on a scale of 100 million metric tons, a portion of which is fragmented into micro-and nanoplastics. These fragments are often colonized by bacterial species in marine environments, possibly contributing to the biodegradation of such materials. However, further investigations are necessary to determine the impact of abiotic polymer weathering on biofilm adhesion, as well as the specific biofilm formation strategies employed by marine isolates. Here, we evaluate deep-sea sediment bacterial isolates for biofilm adhesion, extracellular matrix production, and polymer degradation ability. Our study focuses on high-density polyethylene (HDPE) fragments for their high durability and environmental persistence, subjecting fragments to abiotic weathering prior to bacterial colonization. Marine isolates identified as Pseudomonas sp. and Lysinibacillus sp. exhibited decreasing biofilm formation on weathered HDPE, especially over the first 24 h of incubation. This effect was countered by increased extracellular matrix production, likely improving cell adhesion to surfaces roughened by abiotic degradation. These adhesion strategies were contrasted with a reference Pseudomonas aeruginosa strain, which displayed high levels of biofilm formation on non-weathered HDPE and lower extracellular matrix production over the first 24 h of incubation. Furthermore, our results suggest that an increase in biofilm biomass correlated with changes to HDPE structure, indicating that these strains have a potential for biodegradation of plastic fragments. Therefore, this work provides a detailed account of biofilm formation strategies and bacteria-plastic interactions that represent crucial steps in the biodegradation of plastic fragments in marine environments.

No abstract

No abstract