This study analyzed the bond strength (BS) of HEMA versus HEMA-free self-etch adhesive systems to dentin. The occlusal surface of 20 third molars was removed and the dentin was abraded with 600-grit silicon carbide paper. The teeth were randomly assigned to 4 groups (n=5) and restored with GO, Adper SE Plus, OptiBond All-In-One, and Clearfil 3S Bond adhesive systems and Filtek Z350 composite. After light curing (600 mW/cm²), the teeth were stored in distilled water at 37ºC for 24 h and were sectioned in the mesiodistal and buccolingual directions to obtain sticks (0.8 mm²). The sticks were subjected to tensile force using a universal testing machine (0.5 mm/min), and the modes of failure were analyzed by scanning electron microscopy and classified as adhesive, cohesive, or mixed. The BS data (in MPa) were treated using one-way ANOVA and Tukey's tests at 5% significance. GO presented the lowest mean bond strength value (10.57 ± 3.72) and differed significantly from the other materials (p=0.001), which, in turn, presented statistically similar results (p>0.05) among themselves: Adper SE Plus (29.08 ± 8.93), OptiBond All-In-One (28.36 ± 6.49), and Clearfil 3S Bond (28.62 ± 6.97). Mixed fractures were the most prevalent. It was concluded that the influence of HEMA on BS to dentin was material dependent.

Objective:To analyze the interference of age in the entrance into a public dental care program for infants as well as family behavioral aspects about tooth decay experience in children 0 to 4 years old.Methods:Cross-sectional study involving 465 children who were divided into 3 groups: infants whose mothers joined the program during pregnancy (n=50); infants enrolled in the program during the first year of life (n=230); and infants enrolled in the program between 13 and 18 months old (n=185). The χ2 and Kruskal-Walis tests (95% confidence interval) were used to assess the relationship among variables.Results:There was an association between the age of entrance in the programs and dental caries (p<0.001). A lower prevalence was seen in infants whose mothers joined the program during pregnancy, and among those infants enrolled in the program during the first year of life. The same low prevalence occurred in relation to mothers' commitment to attend follow-up visits with their infants, cariogenic diet, nighttime oral care, duration of night feeding and parents' educational level (p<0.001). Unfavorable socioeconomic conditions (p>0.05) and daily oral care (p=0.214) were common variables in the groups with 99% of occurrence. Commitment to attend follow-up visits, nighttime oral care and parents' educational level (p>0.05) were considered protective factors for dental caries. Cariogenic diet and night feeding were determinant factors to the appearance of dental caries.Conclusion:To promote children oral health it is essential to enroll children in oral health programs and adopt healthy habits as early as possible, besides the adherence of the child to their parents' advice.

Under the conditions of this study, OptiBond FL was the best material to be used for sealing.

Participating in the program positively impacted the infants' oral health.

Aim: To evaluate the bonding durability of materials used as sealants on different dentitions. Methods: Deciduous (D) and permanent (P) molars were divided into four groups (n=5) and sealed with Fluroshield (F) and OptiBond FL (FL). Blocks of composite resin were built, stored in distilled water (24 h/37 °C), sectioned into 0.8 mm 2 and tested at tensile (0.5 mm/min) after 24 h and 6 months. The fractures were observed and classified into adhesive, cohesive or mixed types. The data were analyzed using repeated measures ANOVA and Tukey test (α=5%), with tooth as the experimental unit. Results: There were differences for dentition (p=0.0097), dental sealant (p=0.0019) and time (p=0.0001). At 24h the highest bond strength was observed for OptiBond FL on deciduous and permanent teeth, similar to Fluroshield at both dentitions. After 6 months the bond strength of OptiBond FL did not decrease in the permanent teeth, but decreased similar to Fluroshield in deciduous teeth, the bond strength of Fluroshield decreased similarly in both dentitions. Conclusions: The bond strength of dental sealants varied with the experimental conditions.