Pt/TiO 2 nanosheets with exposed (001) facets were fabricated by a simple hydrothermal route in a Ti(OC 4 H 9 ) 4 -HF-H 2 O mixed solution followed by a photochemical reduction deposition of Pt nanoparticles on TiO 2 nanosheets under xenon lamp irradiation. The prepared samples were characterized by transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, nitrogen adsorption-desorption isotherms, UV-vis diffuse reflectance spectroscopy, and photoluminescence (PL) spectroscopy. Production of • OH radicals on the TiO 2 surface was detected by the PL technique using coumarin as a probe molecule. The effects of Pt loading on the rates of photocatalytic hydrogen production of the as-prepared samples in ethanol aqueous solution were investigated and discussed. The results showed that the photocatalytic hydrogen production rates of TiO 2 nanosheets from the ethanol aqueous solutions were significantly enhanced by loaded Pt on the TiO 2 nanosheets, and the latter with a 2 wt % of deposited Pt exhibited the highest photocatalytic activity. All fluorinated TiO 2 nanosheets exhibited much higher photocatalytic activity than Degussa P25 TiO 2 and pure TiO 2 nanoparticles prepared in pure water due to the synergistic effect of surface fluorination and exposed (001) facets.
Production of hydrogen from photocatalytic water splitting has become an attractive research area due to the possibility of converting solar energy into green chemical energy. In this study, novel NiS nanoparticle (NP) modified CdS nanorod (NR) p-n junction photocatalysts were prepared by a simple two-step hydrothermal method. Even without the Pt co-catalyst, the as-prepared NiS NP-CdS NR samples exhibited enhanced visible-light photocatalytic activity and good stability for H2-production. The optimal NiS loading content was determined to be 5 mol%, and the corresponding H2-production rate reached 1131 μmol h(-1) g(-1), which is even higher than that of the optimized Pt-CdS NRs. It is believed that the assembly of p-type NiS NPs on the surface of n-type CdS NRs could form a large number of p-n junctions, which could effectively reduce the recombination rates of electrons and holes, thus greatly enhancing the photocatalytic activity. This work not only shows a possibility for the utilization of low cost NiS nanoparticles as a substitute for noble metals (such as Pt) in the photocatalytic H2-production but also provides a new insight into the design and fabrication of other new p-n junction photocatalysts for enhancing H2-production activity.
CdS-sensitized Pt/TiO(2) nanosheets with exposed (001) facets were prepared by hydrothermal treatment of a Ti(OC(4)H(9))(4)-HF-H(2)O mixed solution followed by photochemical reduction deposition of Pt nanoparticles (NPs) on TiO(2) nanosheets (TiO(2) NSs) and chemical bath deposition of CdS NPs on Pt/TiO(2) NSs, successively. The UV and visible-light driven photocatalytic activity of the as-prepared samples was evaluated by photocatalytic H(2) production from lactic acid aqueous solution under UV and visible-light (λ ≥ 420 nm) irradiation. It was shown that no photocatalytic H(2)-production activity was observed on the pure TiO(2) NSs under UV and/or visible-light irradiation. Deposition of CdS NPs on Pt/TiO(2) NSs caused significant enhancement of the UV and visible-light photocatalytic H(2)-production rates. The morphology of TiO(2) particles had also significant influence on the visible-light H(2)-production activity. Among TiO(2) NSs, P25 and the NPs studied, the CdS-sensitized Pt/TiO(2) NSs show the highest photocatalytic activity (13.9% apparent quantum efficiency obtained at 420 nm), exceeding that of CdS-sensitized Pt/P25 by 10.3% and that of Pt/NPs by 1.21%, which can be attributed to the combined effect of several factors including the presence of exposed (001) facets, surface fluorination and high specific surface area. After many replication experiments of the photocatalytic hydrogen production in the presence of lactic acid, the CdS-sensitized Pt/TiO(2) NSs did not show great loss in the photocatalytic activity, confirming that the CdS/Pt/TiO(2) NSs system is stable and not photocorroded.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.