In this work, SiO2 nanoparticles were prepared by the sol-gel method after sodium silicate was extracted from rice husk ash (RHA) under various experimental conditions such as types of acids, NaOH concentration, dissolved time, and temperature and used for removal of Fe2+ ions from aqueous solutions. The extracted SiO2 was morphologically and chemically characterized and showed a surface area of 78 m2/g and uniform pores of 2.71 nm, offering high adsorption capacity for Fe2+ ions. The influence of pH, contact time, and amount of adsorbent was studied in order to establish the best conditions for the Fe2+ adsorption and removal. Furthermore, the adsorption data were fitted with an exponential shape curve for all the three variable parameters that affect the adsorption process. The best results were obtained for pH 5, 20 min contact time, and 0.5 g adsorbent dose. The loading adsorption capacity was 9 mg of Fe2+ ions/g SiO2 in the concentration range 0.1–1.0 mgL−1. In addition, the synthesized SiO2 with the size of around 50 nm can be used for specific heavy metal removal and drug delivery, after modification of the SiO2 surface with various functional groups.
Three different sizes of powdered activated carbon (PAC) were added in hybrid anaerobic membrane bioreactors (AnMBRs) and their performance was compared with a conventional AnMBR without PAC in treating palm oil mill effluent. Their working volume was 1 L each. From the result, AnMBRs with PAC performed better than the AnMBR without PAC. It was also found that adding a relatively smaller size of PAC (approximately 100 μm) enhanced the chemical oxygen demand removal efficiency to 78.53 ± 0.66%, while the concentration of mixed liquor suspended solid and mixed liquor volatile suspended solid were 8,050 and 6,850 mg/L, respectively. The smaller size of PAC could also enhance the biofloc formation and biogas production. In addition, the smaller particle sizes of PAC incorporated into polyethersulfone membrane resulted in higher performance of membrane fouling control and produced better quality of effluent as compared to the membrane without the addition of PAC.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.