Concrete is the most widely used material as the main material in construction. As time progresses, human needs also increase, so in this study, wood waste was used into concrete mix with a normal concrete compressive strength value of 20 MPa using aggregate from the Jeneberang River. In this study, using sawdust waste to be utilized in concrete with variations of 0%, 3%, 6% and 9% with the aim of research to find out how the effect of sawdust waste into concrete mix with predetermined variations. The implementation method uses the SNI method by making test objects in the form of cylinders and blocks at the Indonesian Christian University Paul Laboratory. From the results of the research conducted, it was found that the effect of sawdust waste mixed into the concrete mixture showed the value of the compressive strength, tensile strength and flexural strength of the concrete increased by 3% then decreased in variations of 6% and 9% but at the addition of 3% the strength value The compressive strength, tensile strength and flexural strength of concrete decreased compared to normal concrete.
Penelitian ini memanfaatkan limbah karbit sebagai pengganti sebagian semen dalam pembuatan beon yang bertujuan untuk mengetahui nilai optimum penambahan limbah karbit yang berfungsi sebagai pengganti sebagian semen terhadap kuat tekan, kuat tarik belah, dan modulus elastisitas beton. Variasi limbah karbit sebesar 0%, 4%, 6%, dan 8%. Sampel yang digunakan adalah silinder dengan diameter 15 cm dan tinggi 30 cm sebanyak 72 sampel. Pengujian kuat tekan dilakukan pada umur 3 hari, 7 hari, 14 hari, 21 hari, dan 28 hari, dan kekuatan tarik belah dan modulus elastisitas diuji pada umur 28 hari. Hasil pengujian bahan limbah karbit 0% menunjukkan kuat tekan 35,47 MPa, kuat tarik belah 2,59 MPa, dan modulus elastisitas 16957,76 MPa. Variasi 4% limbah karbit, kuat tekan 37.64 MPa, kuat tarik belah 2,66 MPa, dan modulus elastisitas 17180,87 MPa. Variasi 6% limbah karbit, kuat tekan 33.60 MPa, kuat tarik belah 2,50 MPa, dan modulus elastisitas 16635,53 MPa. Variasi 8% limbah karbit, kuat tekan 35.48 MPa, kuat tarik belah 2,50 MPa, dan modulus elastisitas 16429,19 MPa. Hasil penelitian menunjukkan bahwa beton dengan 4% limbah karbit mendapatkan hasil uji paling optimum untuk semua pengujian.
Penelitian tentang teknologi konstruksi terus dikembangkan dengan tujuan memanfatkan limbah karbit dan abu ampas tebu sebagai bahan subtitusi pada semen dalam pembuatan beton mutu normal. Tujuan dari penelitian ini adalah untuk mengetahui nilai dari pengujian kuat tekan, kuat tarik belah dan kuat lentur dengan bahan subtitusi dari limbah karbit dan abu amps tebu 0%, 4%, 8% dan 12%.. Dalam pembuatan benda uji digunakan metode American concrete institute (ACI)s. Pengujian dilakukan pada saat umur beton telah melewati proses masa pemeliharaan 7, 21, dan 21 hari. Dari hasil penelitian ini didapat nilai kuat tekan beton pada umur 28 hari dengan variasi limbah karbit 10% dan abu ampas tebu 0%, 4%, 8% dan 12% adalah 26,044 MPa, 16,042 MPa, 14,626 MPa dan 14,248. Hasil pengujian kuat tarik belah dengan varaiasi limbah 10% dan abu ampas tebu 0%, 4%, 8% dan 12% adalah 2,288 MPa, 1,77 MPa, 1,533 MPa dan 1,486 MPa. Hasil pengujian kuat lentur dengan varaiasi limbah 10% dan abu ampas tebu 0%, 4%, 8% dan 12% yaitu 3,030 MPa, 2,568, 2,414 dan 2,362. Hasil dari penelitian ini menunjukkan semakin tinggi penambahan limbah karbit dan abu ampas tebu maka akan semakin menurun kuat tekan, kuat tarik belah dan kuat tarik lentur beton.
The presence of slag as a result of waste from steel production annually increases. Researchers and environmentalists are very concerned to overcome this problem. Currently steel slag has been studied as a substitute for concrete compilers. The focus of this research is to utilize steel slag as a constituent of porous concrete in direct contact with acidic regions, in this case sulfuric acid and chloride. This test was carried out using 243 samples in testing the compressive strength, tensile strength and pore volume of concrete. Content of steel slag used is 0%, 50% and 80%. In the compressive strength test results for normal curing, sulfate curing and chloride curing showed an increase of 6.49%, 5.71%, 8.28% in the 50% slag content and 10.81%, 10.29%, 17.20% in the 80% slag content. Then in the tensile strength test showed an increase of 7% to 11% in the 50% slag content and 16% to 17% in the 80% slag content. As for the pore volume, the value is in range from 17% to 19%. These results indicate that slag can be used as a substitute for aggregate on porous concrete with compressive strength ranging from 10 MPa to 19 MPa.
Bahan penyusun utama dari pembuatan semen adaIah calsium carbonat. Pada pencampuran beton bahan yang dapat digantikan sebagai bahan yang dapat dipakai sebagai pengganti sebagian semen adaIah kaIsium karbonat. Maksud tujuan dari peneIitian ini ialah mengetahui kuat tekan, kuat tarik beIah, dan kuat Ientur beton yang menggunakan kaIsium karbonat sebagai bahan pengganti sebagian semen pada beton mutu tinggi. Metodologi peneIitian dimulai dari pemeriksaan karakteristik agregat, kaIsium karbonat, serta mix design (SNI 03-2834-200), pembuatan benda uji siIinder dan baIok. HasiI peneIitian yang telah diIakukan menunjukkan bahwa pengaruh kekuatan beton pada umur 28 hari yang menggunakan kaIsium karbonat sebagai substitusi semen pada peneIitian menunjukan bahwa persentase penurunan kuat tekan beton sebesar 1,70 %, kuat tarik beIah sebesar 2,76 %, dan kuat Ientur sebesar 17,95 %. Komposisi campuran beton dengan menggunakan kaIsium karbonat sebagai substitusi semen menunjukkan bahwa semakin tinggi persentase variasi kaIsium karbonat akan mengurangi niIai mutu beton.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.