Collagen has shown promise as a bioink for extrusion-based bioprinting, but further development of new collagen bioink formulations is necessary to improve their printability. Screening these formulations by measuring print accuracy is a costly and time consuming process. We hypothesized that rheological properties of the bioink before, during, and/or after gelation can be used to predict printability. In this study, we investigated the effects of riboflavin photocrosslinking and pH on type I collagen bioink rheology before, during, and after gelation and directly correlated these findings to the printability of each bioink formulation. From the riboflavin crosslinking study, results showed that riboflavin crosslinking increased the storage moduli of collagen bioinks, but the degree of improvement was less pronounced at higher collagen concentrations. Dots printed with collagen bioinks with riboflavin crosslinking exhibited smaller dot footprint areas than those printed with collagen bioinks without riboflavin crosslinking. From the pH study, results showed that gelation kinetics and final gel moduli were highly pH dependent and both exhibited maxima around pH 8. The shape fidelity of printed lines was highest at pH 8-9.5. The effect of riboflavin crosslinking and pH on cell viability was assessed using bovine chondrocytes. Cell viability in collagen gels was found to decrease after blue light activated riboflavin crosslinking but was not affected by pH. Correlations between rheological parameters and printability showed that the modulus associated with the bioink immediately after extrusion and before deposition was the best predictor of bioink printability. These findings will allow for the more rapid screening of collagen bioink formulations.

The properties of electrospun fibrous scaffolds, including degradation, mechanics and cellular interactions, are important for their use in tissue engineering applications. Although some diversity has been obtained previously in fibrous scaffolds, optimization of scaffold properties relies on iterative techniques in both polymer synthesis and processing. Here, we electrospun candidates from a combinatorial library of biodegradable and photopolymerizable poly(β-amino ester)s (PBAEs) to show that the diversity in properties found in this library is retained when processed into fibrous scaffolds. Specifically, three PBAE macromers were electrospun into scaffolds and possessed similar initial mechanical properties, but exhibited mass loss ranging from rapid (complete degradation within ∼2 weeks) to moderate (complete degradation within ∼ 3 months) to slow (only partial degradation after 3 months). These trends in mechanics and degradation mimicked what was previously observed in the bulk polymers. Although cellular adhesion was dependent on the polymer composition in films, adhesion to scaffolds that were electrospun with gelatin was similar on all formulations and controls. To further illustrate the diverse properties that are attainable in these systems, the fastest and slowest degrading polymers were electrospun together into one scaffold, but as distinct fiber populations. This dual-polymer scaffold exhibited behavior in mass loss and mechanics with time that fell between the single-polymer scaffolds. In general, this work indicates that combinatorial libraries may be an important source of information and specific polymer compositions for the fabrication of electrospun fibrous scaffolds with tunable properties.