No abstract

The microbiologically influenced corrosion (MIC) is a very dangerous process, which affects the oil industry. The activity and microorganisms' growth at the pipelines steel cause surface modifications, which can induce a more complex corrosion process. The biocide evaluation for the MIC decrease has been normally based upon microbiological tests, and just a few references mention alternating methods which can be used as criteria for their evaluation. In this work, a commercial biocide was tested, using different electrochemical laboratory techniques, to determine its effect upon a biofilm generating bacteria consortium.Using microbiological techniques, the biocide lethal concentration was determined, and a concentration of 200 ppm was used to kill completely the consortium population in both, plancktonic and sessile parts. The electrochemical techniques: Polarisation Resistance (PR) and Electrochemical Impedance Spectroscopy (EIS), allowed describing the corrosion process associated to the microbial consortium and the biocide effect upon it.

During the characterization of sediments formed in pipelines transporting hydrocarbons, the knowledge of the microbiological diversity becomes very interesting, especially when it is related to microbiologically influenced corrosion (MIC). The presence of microorganisms is considered as one of the factors that affect the corrosion processes occurring at the pipeline; therefore, their corrosiveness must be determined. In this way, the identification of new species affecting the MIC processes is still considered relevant. In this work, the effect of Clostridium celerecrescens upon the corrosion of API KL 52 steel was evaluated. This microorganism was isolated and identified from the sediments collected during the inner cleaning procedures of a gas pipeline. The polarization resistance (PR) and electrochemical impedance spectroscopy (EIS) techniques were considered to estimate the microorganism behavior during the corrosion process. The results were complemented with a metal surface analysis, using a scanning electron microscope (SEM). The resistance values induced by the presence of the microorganisms clearly indicated that C. celerecrescens has an effect on the corrosion process occurring at the API XL 52 steel surface.

The high number of leak events that took place in recent years at a 25.4 cm (10") Ø pipeline transporting anhydrous liquid ammonia, located in the Southeast of Mexico, was the main reason to carry out a number of field studies and laboratory tests that helped establish not only the failure causes but also mitigation and control solutions. The performed activities included direct evaluation at failure sites, total repair programs, metallographic studies and pipeline flexibility analyses. The obtained results were useful to conclude that the failures obeyed a cracking mechanism by Stress Corrosion Cracking (SCC) which was caused by the combined effect of different factors: high stress resistance, high hardness of the base metal with a microstructure prone to brittleness and residual strains originated during the pipeline construction. From the operative, logistic and financial standpoints, it is not feasible to release the stress of approximately 22 km of pipeline. Therefore, the only viable solution is to install a new pipeline with suitable fabrication, construction and installation specifications aimed at preventing the SCC phenomenon.

The Electrochemical Impedance Technique was used to evaluate the influence of a microbial consortium, isolated from a gas pipeline, upon API XL52 steel corrosion rate. The bacteria growth exhibited two different kinetics behavior, one for the plancktonic and the other for the sessile phase. The sessile bacteria were found to be the main responsible for the corrosion rate increment observed during the experiments and no relationship between the plancktonic microorganisms and the corrosion rate increment was found.The diagrams obtained from the electrochemical impedance measurements, indicated a biofilm formation and that the system changed from activation to diffusion control. Although the system was under diffusion control, an increment on the corrosion rate was detected, and a localized corrosion process was induced. The results were complemented with some surface analysis using Scanning Electron Microscopy.