The melting and crystallization behaviour of undrawn poly(ethy1ene terephthalate)nylon 6 biconstituent fibers (BCF) have been investigated by DSC measurements. A decrease of the internal AT between the temperature of the glass transition and the temperature of the cold crystallization has been found. Changes of the temperature of the melt crystallization of the two components depending on the blend ratios (e. g. the phase morphology) have been also observed. These effects have been explained by an interface physical interaction which changes the degree of order of the molecules inside the phases. A relation between the decrease in AT of the PETP component and the maximum draw ratio A , , , , = of the BCF has been established. It is supposed that the change in AT causes the occurrence of local tensions and the initial formation of microcracks in the PETP phase which lead to a decrease of La.
ZUSAMMENFASSUNG:Das Schmelz-und Kristallisationsverhalten von unverstreckten Polyethylenterephthalat-Nylon 6-Zweikomponentenfasern wurde mit Hilfe von DSC-Messungen untersucht. Es wurde eine Abnahme des Intervalls AT zwischen der Glasubergangstemperatur und der Temperatur der kalten Kristallisation gefunden. Es wurden auch hderungen der Temperatur der Schmelzkristallisation der beiden Komponenten beobachtet, die von den Mischungsanteilen abhtingen (z. B. Phasenmorphologie). Diese Effekte wurden mit einer physikalischen Grenzflachenwechselwirkung erklart, die den Ordnungsgrad der Molekiile innerhalb der Phase iindert. Eine Beziehung zwischen der Abnahme von AT der PETP Komponente und des Verstreckungsgradmaximums, Lm, von Zweikomponentenfasern wurde festgestellt. Es wird vermutet, da8 die Anderung von AT das Auftreten von lokalen Spannungen und den Beginn von Mikrorissen in der PETP-Phase verursacht, was zu einer Abnahme von A, , , , = fuhrt.
Mittels Kapillarviskosimetrie wurde das FlieDverhalten van Schmelzen aus Polyethylenterephthalat, Polycaproamid und ihren Mischungen (80 :20 Masse-%) in Anwesenheit van 0,02 bis 0,80 Masse-% N,N'-Ethylen-bis-stearamid bei Scherspannungen van 8,O . lo3 bis 1 , 4 . l o 5 Pa im Temperaturbereich van 543 bis 568 K untersucht. Die viskoelastischen Eigenschaften der Polymerschmelzen wurden durch die berechneten Anfangswerte der Viskositat, des Koeffizienten der Normalspannung und des Moduls der Hochelastizitat beschrieben. 0 peofiozuuecicux ceolicmsax aucnepcuic pacnnasos noau3~unexmepe$mafiama u noauicanpoaMuda s npucymcmsuu ne6onbyux icofiuuecme N. N'-amunen-Buc-crneapuxa~uaa On the rheological behaviour of melt dispersions of poly(ethy1ene terephthalate) and polycaproamide in the presence of small additions of N,N'-ethylene-bis-stearamide The melt flow behaviour of poly(ethy1ene terephthalate), polycaproamide, and their blend (80:20 mass-%) in the presence of 0,02 to 0,80 mass-% N,N' ethylene-bis-stearamide under shear stress from 8,O . lo3 t o 1,4 . lo5 Pa has been investigated in the temperature range from 543 to 568 K by means of capillary viscosimetry. The viscoelastic properties of the polymer melts are described by means of the analytically defined values of viscosity, normal stress coefficient and high-elasticity module under zero shear rate.
Untersuchungen zur Anwendbarkeit der IR-Spektroskopie zur Bestimmung des Kristallinitatsgrades der Einzelkomponenten in PETP-PA-6-Bikomponentenfasern werden beschrieben. Es wird gezeigt, daB die IR-Banden 435 cm-1 (PETP) und 585 cm-l (PA-6) nicht von Absorptionen der anderen Komponente gestort werden. HIT-cnexmpocxonuwmoe onpeaenenue cmenenu tcpucmamuunocmu xo.wnonenmoe e eoJboxnax 6u~~o.wnonenmnoii cuemefib5 n o n u 3 m~e n m e p e~m a~m -~i o n u~u a OIIMCaHbI IzCCJEaOBaHUn no ~PHMCHkiMOCTIi HK-CnCKTpOCItOIIllM RJIFI Onpe~eJIeEMfI CTCIIeHM KPMCTaJIJIEIYHOCTM OTneJIbHbIX KOMIIOHeHTOB B ~I~T~-~A -~-~M K O M~O H~H T H~X BOJIOKHaX. nOKaaaH0, YTO H a klK-nOJIOCkd 435 CM-l (113Tm) M 585 CM-' (rIA-6) He IIOBJILIHIOT nOr2'IO~eHlifI ApyrOrO KOMlIOHeHTa. I R spectroscopic determination of the degree of crystallinity o f components in poly(ethy1ene 1erephthalate)-polyamide bicomponent fibres I R spectroscopy was found to be applicable for determining the degree of crystallinity of the components in PETP/PA-6 bicomponent fibres. The I R bands a t 435 cm-' (PETP) and 585 cm-' (PA-6) do not disturb each other.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.