Using direct sulfation of cellulose, we prepared sulfated cellulose (CS) with various degrees of substitution of sulfate groups (DS), which we used as dopants for PEDOT. PEDOT/CS were prepared via in situ chemical oxidative polymerization of 3,4-ethylenedioxythiophene (EDOT) in an aqueous CS solution. Films of the obtained PEDOT/CS were formed using spin-coating. As a reference, a PEDOT/PSS film was also formed. The electrical conductivity of the PEDOT/CS film with a DS of 1.03 was 0.576 S m À1 . In contrast, the electrical conductivity of the PEDOT/PSS film was 0.0153 S cm À1 . Using Raman spectroscopy, we found that the 1400 and 1500 cm À1 bands correspond to the C a QC b vibrations in the five-member PEDOT ring. Compared with the band of the PEDOT/PSS film, the band of the PEDOT/CS film red-shifted from 1437 to 1433 cm À1 and narrowed. We attributed the increased electrical conductivity of the PEDOT/ CS film to a greater proportion of the quinoid structure than in PEDOT contained in PEDOT/PSS.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.