In industrially relevant Cu/ZnO/Al2 O3 catalysts for methanol synthesis, the strong metal support interaction between Cu and ZnO is known to play a key role. Here we report a detailed chemical transmission electron microscopy study on the nanostructural consequences of the strong metal support interaction in an activated high-performance catalyst. For the first time, clear evidence for the formation of metastable "graphite-like" ZnO layers during reductive activation is provided. The description of this metastable layer might contribute to the understanding of synergistic effects between the components of the Cu/ZnO/Al2 O3 catalysts.

No abstract

Galvanic replacement reactions provide a simple and versatile route for producing hollow nanostructures with controllable pore structures and compositions. However, these reactions have previously been limited to the chemical transformation of metallic nanostructures. We demonstrated galvanic replacement reactions in metal oxide nanocrystals as well. When manganese oxide (Mn3O4) nanocrystals were reacted with iron(II) perchlorate, hollow box-shaped nanocrystals of Mn3O4/γ-Fe2O3 ("nanoboxes") were produced. These nanoboxes ultimately transformed into hollow cagelike nanocrystals of γ-Fe2O3 ("nanocages"). Because of their nonequilibrium compositions and hollow structures, these nanoboxes and nanocages exhibited good performance as anode materials for lithium ion batteries. The generality of this approach was demonstrated with other metal pairs, including Co3O4/SnO2 and Mn3O4/SnO2.

A one-pot, hydrothermal synthesis of nitrogen and sulfur dual doped carbon aerogels is presented, derived from our previously published hydrothermal carbonization approach. Two co-monomers, S-(2-thienyl)-L-cysteine (TC) and 2-thienyl carboxaldehyde (TCA), were used for sulfur incorporation, giving rise to distinct morphologies and varying doping levels of sulfur. Nitrogen-doping levels of 5 wt% and sulfur-doping levels of 1 wt% (using TCA) to 4 wt% (using TC) were obtained. A secondary pyrolysis step was used to further tune the carbon aerogel conductivity and heteroatom binding states. By comparing solely nitrogen-doped with nitrogen- and sulfur-doped carbon aerogels, it was observed that the presence of sulfur improves the overall electrocatalytic activity of the carbon material in both basic and acidic media. This study of the synergistic effect of combined sulfur- and nitrogen-doping in the catalysis of the “oxygen reduction reaction” (ORR) is expected to be significant to future research concerning the improvement of heterogeneous, metal-free, carbon-based catalysts

Active and highly stable oxide-supported IrNiO(x) core-shell catalysts for electrochemical water splitting are presented. IrNi(x)@IrO(x) nanoparticles supported on high-surface-area mesoporous antimony-doped tin oxide (IrNiO(x)/Meso-ATO) were synthesized from bimetallic IrNi(x) precursor alloys (PA-IrNi(x) /Meso-ATO) using electrochemical Ni leaching and concomitant Ir oxidation. Special emphasis was placed on Ni/NiO surface segregation under thermal treatment of the PA-IrNi(x)/Meso-ATO as well as on the surface chemical state of the particle/oxide support interface. Combining a wide array of characterization methods, we uncovered the detrimental effect of segregated NiO phases on the water splitting activity of core-shell particles. The core-shell IrNiO(x)/Meso-ATO catalyst displayed high water-splitting activity and unprecedented stability in acidic electrolyte providing substantial progress in the development of PEM electrolyzer anode catalysts with drastically reduced Ir loading and significantly enhanced durability.