Studies of stress corrosion in X12Cr13 and X20Cr13 steels used for rotor blades of steam turbines have been conducted for determining the average rate of corrosion cracking development da / dt. Specimens were exposed to the salt mist environment of 1,2 ppm NaCl concentration in temperature of 60° C. The research environment represents the initial condensate of humidity from 3÷4%. Average rate of corrosion cracking development for specimens of the X12Cr13 is by 0,005 µm/h higher from specimens of the X20Cr13 steel. Course of the corrosion cracking initiation depends to a high degree on metal structure, and probably the close value of cracking propagation rate depends on the similar structure of those steels – high-tempered martensite with carbides at grain boundaries.

STRESZCZENIE W artykule zaprezentowano proces odwzorowywania właściwości elementów wirujących wytwornicy spalin silnika turbinowego LM 2500 przy użyciu oprogramowania CAD. Przedstawiono również porównanie częstotliwości rezonansowych obliczonych w wyniku symulacji oraz uzyskanych w trakcie pomiarów na rzeczywistym obiekcie. Artykuł zawiera poszczególne etapy odwzorowywania geometrii, począwszy od określania wymiarów rzeczywistego obiektu, poprzez analizę dokumentacji aż do procesu modelowania silnika w programie CAD. Słowa kluczowe: modelowanie, częstotliwości rezonansowe, silnik turbinowy, order tracking.

No abstract

The paper presents results of measurements conducted during multi-stage studies on injectors of WOLA 72H6 engine. The research was conducted to determine the technical condition of the injectors during their operation. As a result of the injector modeling in the CAD environment, the resonant frequencies of the examined element were obtained. The next stage of the study was a stand-alone tests with the simultaneous recording of vibration parameters. The aim of records was to link the vibration parameters with the technical condition of the tested injectors. The study series was finished with measurements on a real object test stand.