In reliability testing of components for PV modules an always remaining question is about material (in)compatibilities and synergistic effects and thus, how results of singly tested materials correlate with materials aged within PV modules. Testing of single materials would simplify sample preparation, reduce costs and offer more testing options. Therefore the main objective of this study was to compare the aging behavior of single backsheets with that of backsheets incorporated within PV modules. Four different types of backsheets were chosen, all of them comprising of polyethylene terephthalate (PET) core layers, but differing outer protection layers. Test modules using identical components, varying only in the type of backsheet used were produced and damp heat aged (85 C/85% RH 2000 h). The results revealed no influence of the PV module lamination on the thermal characteristics of the polymeric backsheets. Even after DH aging, differences between single and module laminated backsheets were negligible. Degradation effects of PET could be detected for all aged sheets by thermal analysis and were confirmed by tensile tests and rheological measurements. Thus, it can be stated that testing of single PET based backsheets under DH aging conditions is a practicable way to investigate the applicability of a new backsheet.
The influence of the type of backsheet on the electrical performance of test modules was evaluated before and after increasing time of accelerated ageing (damp heat [DH] exposure). Besides the measurement of the electrical power of the modules and the performance of the cells by electroluminescence, the ageing-induced changes within the polymeric encapsulate and backsheets were investigated by means of vibrational spectroscopy and by thermo analytical methods. In addition, the permeability of the backsheets in the original and aged state was determined. This wide set of test parameters and methods allowed for the detection of correlations between (i) physical and chemical properties as well as their ageing-induced changes of the materials and (ii) the module performance. A clear dependence of the relative loss in power output upon exposure under DH conditions for 2000 h could be observed for a set of identical test modules varied in composition only in the type of back cover used. While the modules containing gas-tight backsheets and glass experienced only little loss in the relative power output, some modules with permeable backsheets showed a significant relative decrease in the power output and fill factor in dependence of the backsheet type used. Cell degradation could be visualised by recording electroluminescence images before and after the accelerated ageing test. The permeation properties of the backsheet used and their ageing-induced changes seem to have an influence on the module performance. However, the absolute values neither of the water vapour transmission rate (WVTR) nor of the oxygen transmission rate (OTR) are directly linked to the loss in power output upon accelerated ageing under DH conditions. It could be shown that the ageing-induced changes (relative transmission rates) between WVTR and OTR can be correlated with the module performance. These ageing-induced changes in the permeation behaviour of the backsheets can be explained by (i) physical changes (e.g. post-crystallisation, changes in the crystal structure or the crystalline microstructure) and (ii) chemical ageing effects such as a decrease in the molecular mass of the polyester (PET) polymer chains because of hydrolytic polymer degradation leading to a change in the crystallisation behaviour of PET. Hydrolytic degradation (= chemical ageing) of the PET core layer was observed (with varying extent) for all PET-based backsheets and can, thus, not be directly correlated with the loss in performance of the corresponding test modules. The physical ageing effects, however, were detected only for those backsheets showing (i) strong deviating changes in the relative permeation rates for oxygen and water vapour upon accelerated ageing and (ii) a clear loss in electrical performance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.