Aims. This study aimed to evaluate the effect of 2.5% and 7.5% copper oxide (CuO) and titanium dioxide (TiO2) nanoparticles on the antimicrobial activity of thermocycled polymethyl methacrylate (PMMA) denture base material against standard strains of yeast and bacteria species. Material and Methods. In this in vitro study, 150 disk-shaped (10 × 2 mm) specimens of heat-cured PMMA were prepared and divided into five groups (n = 30) to be reinforced with 2.5% CuO, 7.5% CuO, 2.5% TiO2, or 7.5% TiO2 nanoparticles and a control group (without nanoparticle). The specimens were thermocycled, and their antimicrobial activity was assessed against standard strains of yeast including Candida albicans and C. dubliniensis and oral bacteria species including Streptococcus mutans, S. sobrinus, S. salivarius, and S. sanguis. Data were analyzed with ANOVA and Tukey’s post hoc tests (α = 0.05). Results. Both concentrations of CuO and TiO2 nanoparticles had significant antimicrobial activity against S. salivarius, S. sanguis, and C. dubliniensis compared with the control group (
P
< 0.05). Significant differences existed between both 2.5% (
P
= 0.006) and 7.5% CuO (
P
= 0.005) and the control group against S. mutans. However, TiO2 groups were not significantly different from the control group against S. mutans. Concerning C. albicans, 7.5% TiO2 was the only nanoparticle with significantly higher antimicrobial activity compared with the control group (
P
= 0.043). Conclusions. Both concentrations of CuO and TiO2 were effective antimicrobial agents against S. salivarius, S. sanguis, and C. dubliniensis, and the concentration of CuO was effective against S. mutans. Yet, TiO2 was not much effective. Regarding C. albicans, only 7.5% TiO2 showed efficient antimicrobial activity.
Objectives Inner carious dentin is specified with decreased minerals and collagen cross-links but without protein denaturation. Current minimally invasive dentistry concepts recommend removal of only the outer layer of carious dentin and biomodification of repairable inner carious dentin. The present study aims to investigate the possibility of functional repair of this layer using silver diamine fluoride (SDF) and grape seed extract (GSE).
Materials and Methods Molar teeth with occlusal caries were used to prepare caries-affected dentin specimens for hardness and elastic modulus measurements. The specimens of each test were divided randomly into four equal groups. In the GSE group, the specimens were immersed in 6.5% GSE solution for 10 minutes. In the SDF group, the specimens underwent a topical application of a 30% SDF. In the GSE+SDF group, first the specimens were immersed in GSE and then exposed to SDF. In the SDF+GSE group, first SDF was applied and then the specimens were immersed in GSE. Microhardness measurements were taken at baseline and after treatment. A control group with distilled water treatment was also prepared for elastic modulus measurements.
Statistical Analysis One-way analysis of variance and post-hoc tests were used for statistical analysis.
Results There were significant differences in H1-H0 (final hardness—baseline hardness) among the groups. Baseline and final hardness of each group was also significantly different (SDF>SDF+GSE>GSE>GSE+SDF). Elastic modulus of SDF and SDF+GSE increased compared to the control group.
Conclusions SDF and SDF+GSE treatment can be recommended to increase hardness and elastic modulus of caries-affected dentin.
The aim of this study was to evaluate the effect of silver diamine fluoride and grape seed extract on the microstructure and mechanical properties of carious dentin following exposure to acidic challenge. Ninety-eight molars with occlusal caries were used. In the control group the specimens were kept in distilled water. In the GSE group, the specimens were immersed in 6.5% grape seed extract solution for 30 minutes. In the SDF group, the specimens were immersed in 30% SDF solution for 4 minutes. In the GSE+SDF group, the specimens were immersed in 6.5% grape seed extract solution for 30 minutes and then exposed to 30% SDF solution for 4 minutes. All the groups underwent pH cycling model for 8 days. Microhardness measurements were taken at the baseline before surface treatments and after pH cycling. Elastic modulus was measured, after pH cycling. In the control group, the final hardness was significantly lower than the initial hardness (P = 0.001). In the SDF group, the final hardness was significantly higher than the initial hardness (P < 0.001). There was no significant difference between the initial and final hardness values in the GSE and GSE + SDF groups (p = 0.92, p = 0.07). The H 1-H 0 in the SDF group was significantly higher than the other groups (P<0.05). Moreover, elastic modulus of the experimental groups except GSE+SDF group was significantly higher than control. The highest mean elastic modulus was detected in the SDF group (P<0.001). The use of SDF and GSE prior to the acid challenge improved mechanical properties. Microstructural investigation, using scanning electron microscope showed dentin structure protection against acid challenges with SDF treatment and collagen matrix stabilization with GSE treatment. However combined use of these agents was not beneficious.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.